Toyobo Vylopet® EMC605 PET/PBT Blend
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo Vylopet® EMC605 PET/PBT Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: Flame retardant V-0 UL 94 classApplications: glossy surface componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, chemical & weather resistance, and processability.Information provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 47.0 MPa | 6820 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Flexural Yield Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Compressive Yield Strength | 54.0 MPa | 7830 psi | ASTM D695 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 18 | 18 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 210 V | 210 V | IEC test |
Users viewing this material also viewed the following:
- DSM Somos® 8120 Epoxy Photopolymer (discontinued **)
- Hong Kun Group 4-Bromo-2-fluoroaniline Pharmaceutical Intermediate
- Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Conditioned)
- Gouda Vuurvast AK 65 A Dense Refractory Brick
- Sharadaa Ceramics REFCAST C SUPER High Alumina Castables
- SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC
- ExxonMobil Enable™ 20-10CB Metallocene Polyethylene Resin (European Grade)
- Fainplast Compounds HG 83 Flexible PVC, Sheathing for High Temperatures
- ExxonMobil Escorene® LD 720.62 Specialty Film Resin
Copyright © lookpolymers.com All Rights Reserved