Tra-Con Tra-Bond 516H02 Fiber Optic Adhesive
| Category | Polymer , Adhesive , Thermoset , Filled/Reinforced Thermoset |
| Manufacturer | Tra-Con, Inc. |
| Trade Name | Tra-Bond |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tra-Con Tra-Bond 516H02 Fiber Optic Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRA-BOND 516H02 is a low viscosity, room temperature or low temperature curing fiber optic adhesive with good stress relief, high adhesion, and low shrinkage upon cure. TRA-BOND 516H02 contains very fine filler (< 1 micron) for low CTE and aids in maintaining fiber alignment.Information provided by Tra-Con Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | Cured |
| Viscosity | 4000 cP | 4000 cP | Mixed (cp #40, 2.5 rpm) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | Overnight @ RT |
| Adhesive Bond Strength | 26.9 MPa | 3900 psi | Lap shear, alum to alum, 1 hr @ 65°C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 48.0 µm/m-°C @Temperature 20.0 °C |
26.7 µin/in-°F @Temperature 68.0 °F |
Alpha 1 |
| Glass Transition Temp, Tg | 50.0 °C | 122 °F | Ultimate Tg; TMA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 1440 - 2160 min | 24.0 - 36.0 hour | At RT |
| 60.0 min @Temperature 65.0 °C |
1.00 hour @Temperature 149 °F |
||
| 180 - 240 min @Temperature 40.0 °C |
3.00 - 4.00 hour @Temperature 104 °F |
||
| Pot Life | 25 min | 25 min |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | Hardener |
| Tan | Resin |