Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ISO 2039 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Elongation at Break | 4.6 % | 4.6 % | ISO 527-1/-2 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527-1/-2 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 42.0 µm/m-°C | 23.3 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | HB @Thickness 0.860 mm |
HB @Thickness 0.0339 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+11 ohm-cm | 8.00e+11 ohm-cm | IEC 60093 |
| Dielectric Strength | 36.0 kV/mm @Thickness 1.00 mm |
914 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Users viewing this material also viewed the following:
- Mar-Bal MB1000-15 Thermoset Polyester Composite Molding Compound
- LATI Laramid G/30-V0HF1 PPA, 30% Glass Fiber Reinforced, Flame Retardant
- Schott OG570 Long Pass Filter
- Sylvin Technologies 9980-65 Natural PVC Molding Compound
- SK Chemicals SKYPET® BB8055 Specially Formulated PET Resin
- Chengdu Polyster RPM650 Flame Retardant Masterbatch
- EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30
- CP-Polymer-Technik Wellamid® 6600 GV 40 HWCP 40% Glass Fiber Nylon 66, Heat Stabilized, Dry
- Cheng Yu Plastic IPS600UV Flame Retardant HIPS
- Techmer ES HiFill FR® PPO/HIPS GF20 BK 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved