Unitika A3130 PA6, 35% Mineral Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A3130 PA6, 35% Mineral Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ISO 2039 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
| Elongation at Break | 3.8 % | 3.8 % | ISO 527-1/-2 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527-1/-2 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+11 ohm-cm | 5.00e+11 ohm-cm | IEC 60093 |
Users viewing this material also viewed the following:
- Nye Lubricants 231L (SO) Synthetic Oil
- Polykemi AB POLYfill PPC T1035 Polypropylene Copolymer, Mineral Reinforced
- Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) (Unverified Data**)
- Samyang Tramid® 210P Polyamide, High Productivity
- Solvay RHODAPHOSE® DI-TERT BUTYL POTASSIUMPHOSPHATE Phosphorus Derivative
- Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH
- Assab Steels EM38 Steel for Plastic Molds
- Alliance S-26H Samarium Cobalt Magnetic Material
- Ineos HB111R Polyethylene Copolymer
- CeramTec SL200B Silicon Nitride
Copyright © lookpolymers.com All Rights Reserved