Unitika CX-2500 PA6, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	Unitika
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika CX-2500 PA6, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Transparent nylonInformation provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.11 g/cc	0.0401 lb/in³	ISO 1183
Water Absorption	0.70 % @Time 86400 sec	0.70 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	1.3 %	1.3 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Thickness 3.20 mm	0.0070 in/in @Thickness 0.126 in
Linear Mold Shrinkage, Transverse	0.013 cm/cm @Thickness 3.20 mm	0.013 in/in @Thickness 0.126 in

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	67.0 MPa	9720 psi	ISO 527-1/-2
Elongation at Break	60 %	60 %	ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	ISO 527-1/-2
Tensile Modulus	2.70 GPa	392 ksi	ISO 527-1/-2
Flexural Strength	113 MPa	16400 psi	ISO 178
Flexural Modulus	2.60 GPa	377 ksi	ISO 178
Charpy Impact Unnotched	8.00 J/cm²	38.1 ft-lb/in²	ISO 179-1
Charpy Impact, Notched	0.200 J/cm²	0.952 ft-lb/in²	ISO 179-1

Thermal Properties	Metric	English	Comments
CTE, linear	77.0 µm/m-°C	42.8 µin/in-°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C	158 °F	ISO 75-1/-2
Flammability, UL94	V-2 @Thickness 0.750 mm	V-2 @Thickness 0.0295 in