Victrex® PEEK 150G / 151G Polyetheretherketone, Unreinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 150G / 151G Polyetheretherketone, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Complex geometries with thin cross sections or long flow lengths, for high strength and stiffness as well as good ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
0.40 %

@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
0.55 %

@Temperature 100 °C
0.55 %

@Temperature 212 °F
immersion; ISO 62-1
Viscosity 140000 cP

@Temperature 400 °C
140000 cP

@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
365°C nozzle, 160°C tool; ISO 294-4
Spiral Flow 220 cm

@Thickness 1.00 mm
86.6 in

@Thickness 0.0394 in
365°C nozzle, 160°C tool
250 cm

@Thickness 1.00 mm
98.4 in

@Thickness 0.0394 in
375°C nozzle, 180°C tool
300 cm

@Thickness 1.00 mm
118 in

@Thickness 0.0394 in
400°C nozzle, 200°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 85

@Temperature 23.0 °C
85

@Temperature 73.4 °F
ISO 868
Tensile Strength, Yield 105 MPa

@Temperature 23.0 °C
15200 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 30 %

@Temperature 23.0 °C
30 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 4.10 GPa

@Temperature 23.0 °C
595 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 13.5 MPa

@Temperature 275 °C
1960 psi

@Temperature 527 °F
ISO 178
20.0 MPa

@Temperature 175 °C
2900 psi

@Temperature 347 °F
ISO 178
90.0 MPa

@Temperature 125 °C
13100 psi

@Temperature 257 °F
ISO 178
175 MPa

@Temperature 23.0 °C
25400 psi

@Temperature 73.4 °F
ISO 178
130 MPa

@Strain 3.50 %
18900 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 3.90 GPa

@Temperature 23.0 °C
566 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 80.0 MPa

@Temperature 120 °C
11600 psi

@Temperature 248 °F
ISO 604
130 MPa

@Temperature 23.0 °C
18900 psi

@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 0.500 kJ/m²

@Temperature 23.0 °C
0.238 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/U
Charpy Impact, Notched 0.420 J/cm²

@Temperature 23.0 °C
2.00 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C

@Temperature <=143 °C
30.6 µin/in-°F

@Temperature <=289 °F
Average below Tg; ISO 11359
140 µm/m-°C

@Temperature >=143 °C
77.8 µin/in-°F

@Temperature >=289 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature <=143 °C
27.8 µin/in-°F

@Temperature <=289 °F
Below Tg; ISO 11359
120 µm/m-°C

@Temperature >=143 °C
66.7 µin/in-°F

@Temperature >=289 °F
Above Tg; ISO 11359
Thermal Conductivity 0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
Along flow; ISO 22007-4
0.290 W/m-K

@Temperature 23.0 °C
2.01 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
Average; ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 156 °C
313 °F
ISO 75A-f
167 °C

@Temperature 200 °C,
Time 14400 sec
333 °F

@Temperature 392 °F,
Time 4.00 hour
ISO 75A-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
147 °C
297 °F
Midpoint; ISO 11357
UL RTI, Electrical 260 °C
500 °F
UL 746B
UL RTI, Mechanical with Impact 180 °C
356 °F
UL 746B
UL RTI, Mechanical without Impact 240 °C
464 °F
UL 746B
Oxygen Index 24 %

@Thickness 0.400 mm
24 %

@Thickness 0.0157 in
ISO 4239
35 %

@Thickness 3.20 mm
35 %

@Thickness 0.126 in
ISO 4239
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 ohm-cm

@Temperature 275 °C
1.00e+9 ohm-cm

@Temperature 527 °F
IEC 60093
1.00e+15 ohm-cm

@Temperature 125 °C
1.00e+15 ohm-cm

@Temperature 257 °F
IEC 60093
1.00e+16 ohm-cm

@Temperature 23.0 °C
1.00e+16 ohm-cm

@Temperature 73.4 °F
IEC 60093
Dielectric Constant 3.1

@Frequency 50000 Hz,
Temperature 23.0 °C
3.1

@Frequency 50000 Hz,
Temperature 73.4 °F
IEC 60250
Dielectric Strength 23.0 kV/mm

@Thickness 2.50 mm
584 kV/in

@Thickness 0.0984 in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.0040

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 365 °C
689 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 °C

@Time 18000 sec
248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
Toxicity Index 0.074
NES 713; CO content
0.15
NES 713; CO<sub>2</sub> content
0.22
NES 713; Total gases