Victrex® PEEK 150GL30 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 150GL30 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour natural/beige.Typical Application Areas: Complex geometries with thin cross sections or long flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications.Information provided by Victrex.
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ASTM D792
Water Absorption 0.11 %
0.11 %
24 hrs; ASTM D570
Water Absorption at Saturation 0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 immersion; ISO 62-1
0.45 %

@Temperature 100 °C
 0.45 %

@Temperature 212 °F
 immersion; ISO 62-1
Viscosity 275000 cP

@Temperature 400 °C
 275000 cP

@Temperature 752 °F
 melt; ISO 11443
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
Melt Flow 16 g/10 min

@Load 5.00 kg,
Temperature 400 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 752 °F
Spiral Flow 13.5 cm

@Thickness 1.00 mm
 5.31 in

@Thickness 0.0394 in
 recommended processing conditions
Mechanical Properties Metric English Comments
Hardness, Shore D 87
87
ISO 868
Tensile Strength at Break 45.0 MPa

@Temperature 275 °C
 6530 psi

@Temperature 527 °F
 ISO 527
65.0 MPa

@Temperature 225 °C
 9430 psi

@Temperature 437 °F
 ISO 527
75.0 MPa

@Temperature 175 °C
 10900 psi

@Temperature 347 °F
 ISO 527
125 MPa

@Temperature 125 °C
 18100 psi

@Temperature 257 °F
 ISO 527
200 MPa

@Temperature 23.0 °C
 29000 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 2.7 %
2.7 %
ISO 527
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527
Flexural Strength 75.0 MPa

@Temperature 275 °C
 10900 psi

@Temperature 527 °F
 ISO 178
120 MPa

@Temperature 175 °C
 17400 psi

@Temperature 347 °F
 ISO 178
230 MPa

@Temperature 125 °C
 33400 psi

@Temperature 257 °F
 ISO 178
290 MPa

@Temperature 23.0 °C
 42100 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 11.5 GPa
1670 ksi
ISO 178
Compressive Strength 55.0 MPa

@Temperature 200 °C
 7980 psi

@Temperature 392 °F
 ISO 604
160 MPa

@Temperature 120 °C
 23200 psi

@Temperature 248 °F
 ISO 604
250 MPa

@Temperature 23.0 °C
 36300 psi

@Temperature 73.4 °F
 ISO 604
Izod Impact, Notched (ISO) 10.5 kJ/m²

@Temperature 23.0 °C
 5.00 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/U
Charpy Impact Unnotched 5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1U
Charpy Impact, Notched 0.750 J/cm²

@Temperature 23.0 °C
 3.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature >=143 °C
 11.1 µin/in-°F

@Temperature >=289 °F
 ISO 11359
20.0 µm/m-°C

@Temperature <=143 °C
 11.1 µin/in-°F

@Temperature <=289 °F
 ISO 11359
45.0 µm/m-°C

@Temperature <=143 °C
 25.0 µin/in-°F

@Temperature <=289 °F
 ISO 11359
110 µm/m-°C

@Temperature >=143 °C
 61.1 µin/in-°F

@Temperature >=289 °F
 ISO 11359
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Average; ISO 22007-4
0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
Along flow; ISO 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 335 °C
635 °F
ISO 75-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
147 °C
297 °F
Midpoint; ISO 11357
UL RTI, Electrical 240 °C
464 °F
UL 746B
UL RTI, Mechanical with Impact 220 °C
428 °F
UL 746B
UL RTI, Mechanical without Impact 240 °C
464 °F
UL 746B
Glow Wire Test 960 °C

@Thickness 50.8 mm
 1760 °F

@Thickness 2.00 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Dielectric Constant 3.3

@Frequency 1000 Hz
 3.3

@Frequency 1000 Hz
3.3

@Frequency 1e+6 Hz
 3.3

@Frequency 1e+6 Hz
Dissipation Factor 0.0040

@Frequency 1e+6 Hz
 0.0040

@Frequency 1e+6 Hz
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 380 °C
716 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Dry Time 3.00 hour

@Temperature 150 °C
 3.00 hour

@Temperature 302 °F
5.00 hour

@Temperature 120 °C
 5.00 hour

@Temperature 248 °F