Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer	Victrex
Trade Name	PEEK
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, color natural/beige.Typical Application Areas: Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®

Physical Properties	Metric	English	Comments
Density	1.51 g/cc	0.0546 lb/in³	Crystaline; ISO 1183
Water Absorption at Saturation	0.30 % @Temperature 23.0 °C	0.30 % @Temperature 73.4 °F	immersion; ISO 62-1
	0.45 % @Temperature 100 °C	0.45 % @Temperature 212 °F	immersion; ISO 62-1
Viscosity	700000 cP @Temperature 420 °C	700000 cP @Temperature 788 °F	melt; ISO 11443
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	405°C nozzle, 190°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	405°C nozzle, 190°C tool; ISO 294-4
Spiral Flow	9.00 cm @Thickness 1.00 mm	3.54 in @Thickness 0.0394 in	405°C nozzle, 190°C tool
	45.0 cm @Thickness 3.00 mm	17.7 in @Thickness 0.118 in	405°C nozzle, 190°C tool

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	30.0 MPa @Temperature 275 °C	4350 psi @Temperature 527 °F	ISO 527
	50.0 MPa @Temperature 175 °C	7250 psi @Temperature 347 °F	ISO 527
	95.0 MPa @Temperature 125 °C	13800 psi @Temperature 257 °F	ISO 527
	170 MPa @Temperature 23.0 °C	24700 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	2.9 %	2.9 %	ISO 527
Tensile Modulus	11.5 GPa	1670 ksi	ISO 527
Flexural Strength	45.0 MPa @Temperature 275 °C	6530 psi @Temperature 527 °F	ISO 178
	75.0 MPa @Temperature 175 °C	10900 psi @Temperature 347 °F	ISO 178
	170 MPa @Temperature 125 °C	24700 psi @Temperature 257 °F	ISO 178
	260 MPa @Temperature 23.0 °C	37700 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	10.0 GPa	1450 ksi	ISO 178
Compressive Strength	35.0 MPa @Temperature 200 °C	5080 psi @Temperature 392 °F	ISO 604
	120 MPa @Temperature 120 °C	17400 psi @Temperature 248 °F	ISO 604
	190 MPa @Temperature 23.0 °C	27600 psi @Temperature 73.4 °F	ISO 604
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	ISO 180/A
Izod Impact, Unnotched (ISO)	65.0 kJ/m²	30.9 ft-lb/in²	ISO 180/U
Charpy Impact Unnotched	7.00 J/cm²	33.3 ft-lb/in²	ISO 179/1U
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	45.0 µm/m-°C @Temperature <=143 °C	25.0 µin/in-°F @Temperature <=289 °F	Average below Tg; ASTM D696
	120 µm/m-°C @Temperature >=143 °C	66.7 µin/in-°F @Temperature >=289 °F	Average above Tg; ASTM D696
CTE, linear, Parallel to Flow	18.0 µm/m-°C @Temperature <=143 °C	10.0 µin/in-°F @Temperature <=289 °F	Below Tg; ASTM D696
	22.0 µm/m-°C @Temperature >=143 °C	12.2 µin/in-°F @Temperature >=289 °F	Above Tg; ASTM D696
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F	Average; ISO 22007-4
	0.350 W/m-K	2.43 BTU-in/hr-ft²-°F	Along flow; ISO 22007-4
Melting Point	343 °C	649 °F	ISO 11357
Deflection Temperature at 1.8 MPa (264 psi)	320 °C	608 °F	ISO 75A-f
Glass Transition Temp, Tg	>= 143 °C	>= 289 °F	Onset; ISO 11357
	150 °C	302 °F	Midpoint; ISO 11357

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	IEC 60093
Dielectric Constant	3.5 @Frequency 1000 Hz	3.5 @Frequency 1000 Hz	IEC 60250
Dielectric Strength	20.0 kV/mm @Thickness 2.00 mm	508 kV/in @Thickness 0.0787 in	IEC 60243-1
Dielectric Loss Index	0.0040 @Frequency 1.00e+6 Hz	0.0040 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	150 V	150 V	IEC 60112

Processing Properties	Metric	English	Comments
Processing Temperature	<= 100 °C	<= 212 °F	Hopper Temperature
Nozzle Temperature	405 °C	761 °F
Mold Temperature	180 - 200 °C	356 - 392 °F
Dry Time	3.00 hour @Temperature 150 °C	3.00 hour @Temperature 302 °F
	5.00 hour @Temperature 120 °C	5.00 hour @Temperature 248 °F