Vyncolit Neopreg Kinel® SK60 L8F Glass Fiber Reinforced Molding Compound

Category Polymer , Thermoset , Epoxy , Epoxy Molding Compound , Filled/Reinforced Thermoset
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name Neopreg Kinel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit Neopreg Kinel® SK60 L8F Glass Fiber Reinforced Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium flow, epoxy based molding compound long glass fiber reinforced with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 0.500 g/cc
0.0181 lb/in³
ISO 60
Density 1.86 g/cc
0.0672 lb/in³
ISO 1183
Water Absorption 0.050 %
0.050 %
ISO 62
Linear Mold Shrinkage 0.00090 cm/cm
0.00090 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 119 MPa
17300 psi
ISO 527-1
Elongation at Break 0.80 %
0.80 %
ISO 527-1
Tensile Modulus 21.0 GPa
3050 ksi
ISO 527-1
Flexural Strength 223 MPa
32300 psi
ISO 178
Flexural Modulus 17.0 GPa
2470 ksi
ISO 178
Compressive Strength 227 MPa
32900 psi
ISO 604
Charpy Impact, Notched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.90 µm/m-°C
4.39 µin/in-°F
TMA
CTE, linear, Transverse to Flow 59.0 µm/m-°C
32.8 µin/in-°F
TMA
Thermal Conductivity 0.560 W/m-K
3.89 BTU-in/hr-ft²-°F
ASTM E1461
Glass Transition Temp, Tg 165 °C
329 °F
Shrinkage -0.0400 %
-0.0400 %
Post Shrinkage; ISO 2577
Electrical Properties Metric English Comments
Dielectric Strength 38.0 kV/mm
965 kV/in
IEC 60243-1
Dissipation Factor 0.022

@Frequency 100 - 1e+6 Hz
0.022

@Frequency 100 - 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60250
Descriptive Properties Value Comments
Color Dark Grey
Molding Method Compression
Injection
Transfer