Vyncolit W5020 Glass Filled Novolac Phenolic

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit W5020 Glass Filled Novolac Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Novolac resin based, glass fiber and glass bead reinforced. High dimensional stability and excellent chemical resistance at high temperatures in hydraulic brake fluids. Used in the ABS system.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 0.670 g/cc
0.0242 lb/in³
ISO 60
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Water Absorption 0.050 %
0.050 %
ISO 62
Linear Mold Shrinkage 0.0036 cm/cm
0.0036 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527-1
Elongation at Break 0.85 %
0.85 %
ISO 527-1
Tensile Modulus 14.0 GPa
2030 ksi
ISO 527-1
Flexural Strength 185 MPa
26800 psi
ISO 178
Flexural Modulus 13.0 GPa
1890 ksi
ISO 178
Compressive Strength 270 MPa
39200 psi
ISO 604
Charpy Impact Unnotched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.0 µm/m-°C
12.2 µin/in-°F
TMA
CTE, linear, Transverse to Flow 44.0 µm/m-°C
24.4 µin/in-°F
TMA
Deflection Temperature at 1.8 MPa (264 psi) >= 188 °C
>= 370 °F
ISO 75 Af
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Shrinkage 0.050 %
0.050 %
Post Shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 3.17e+13 ohm-cm
3.17e+13 ohm-cm
IEC 60093
Surface Resistance 2.41e+13 ohm
2.41e+13 ohm
IEC 60093
Dielectric Strength 36.0 kV/mm
914 kV/in
IEC 60243-1
Comparative Tracking Index 175 V
175 V
IEC 60250
Descriptive Properties Value Comments
Colors Black, Green
Molding Method Compression
Injection
Transfer