Wieland Portadur T Casting Alloy
| Category | Metal , Nonferrous Metal , Precious Metal , Gold Alloy |
| Manufacturer | Wieland |
| Trade Name | Portadur |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wieland Portadur T Casting Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Gold casting alloyApplications: inlays/onlays, crowns, acrylic veneeringDental
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 15.9 g/cc | 0.574 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | 120 | 120 | HV5/30; as cast |
| 150 | 150 | HV5/30; hardened | |
| Tensile Strength, Yield | 230.00 MPa @Strain 0.200 % |
33359 psi @Strain 0.200 % |
as cast |
| 370.00 MPa @Strain 0.200 % |
53664 psi @Strain 0.200 % |
hardened | |
| Elongation at Break | 35 % | 35 % | hardened |
| 39 % | 39 % | as cast | |
| Modulus of Elasticity | 95.0 GPa | 13800 ksi |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Copper, Cu | 8.5 % | 8.5 % | |
| Gold, Au | 77 % | 77 % | |
| Indium, In | 0.20 % | 0.20 % | |
| Iridium, Ir | 0.10 % | 0.10 % | |
| Platinum, Pt | 1.0 % | 1.0 % | |
| Silver, Ag | 13 % | 13 % | |
| Zinc, Zn | 0.20 % | 0.20 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 649 °C | 1200 °F | Preheating Temp. |
| Melt Temperature | 899 - 938 °C | 1650 - 1720 °F | |
| Casting Temperature | 1050 °C | 1920 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | yellow |