Zell-Metall Engineering Plastics Zellamid 1400 (PET)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer Zell-Metall Engineering Plastics
Trade Name Zellamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zell-Metall Engineering Plastics Zellamid 1400 (PET).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zellamid® 1400 is the registered trademark of Zell-Metall’s partly crystalline thermoplastic Polyester based on Polyethylene Terephthalate.This PETP features outstanding dimensional stability, as it is virtually unaffected by ambient moisture. A low coefficient of friction and excellent wear resistance combined with low creep and high modulus make this the choice material for moving parts. Hot water resistance is low.Zellamid® 1400 is produced without centerline porosity. This material exhibits properties which make it suited to particular applications, especially high precision components.Typical applications are components for foodprocessing machines, mandrels, liquid and gas proof parts, electrical engineering and all parts where Acetal’s microporosity in the centerline is not desirable.For friction applications we offer Zellamid® 1400T (PETP with a solid lubricant) which shows a significantly reduced friction coefficient and increased resistance to wear.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
Moisture Absorption at Equilibrium 0.23 %
0.23 %
Saturation at 50% RH; ISO 1110; DIN 53714
Water Absorption at Saturation 0.50 %
0.50 %
23°C; ISO 62; DIN 53495
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
ISO 527; DIN 53455
Elongation at Break 20 %
20 %
ISO 527; DIN 53455
Tensile Modulus 3.20 GPa
464 ksi
ISO 527; DIN 53452
Charpy Impact Unnotched 8.20 J/cm²

@Temperature 23.0 °C
39.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179; DIN 53453
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
double V-notch, rk=1.5 mm; DIN 53753
Dart Drop, Total Energy 80.0 J
59.0 ft-lb
DIN 53443
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Melting Point 255 °C
491 °F
ISO 1218 Method A; DIN 53736
Maximum Service Temperature, Air 100 °C
212 °F
20,000 hours; 50% Tensile Strength; IEC 216; DIN 53446
115 °C
239 °F
5000 hours; 50% Tensile Strength; IEC 216; DIN 53446
160 °C
320 °F
a few hours operation
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
ISO 75; DIN 53461
Deflection Temperature at 1.8 MPa (264 psi) 67.0 °C
153 °F
ISO 75; DIN 53461
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 167; DIN 53482
Dielectric Constant 3.3

@Frequency 1e+6 Hz
3.3

@Frequency 1e+6 Hz
IEC 250; DIN 53483
Dielectric Strength 50.0 kV/mm
1270 kV/in
IEC 243; DIN 53481
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
IEC 250; DIN 53483
Comparative Tracking Index >= 450 V
>= 450 V
KA Method; IEC 112; DIN 53480
>= 600 V
>= 600 V
KC Method; IEC 112; VDE 0303T1
Descriptive Properties Value Comments
Resistance to Wear 2.2 µm/km
DIN-ISO 7148-2; Ra = 0.35 - 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm2, time T > 16 h
VDE Fire Performance ll b
VDE 0304T3