Zell-Metall Engineering Plastics Zellamid 202 (PA 6) at 50% RH

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Zell-Metall Engineering Plastics
Trade Name Zellamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zell-Metall Engineering Plastics Zellamid 202 (PA 6) at 50% RH.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zellamid® 202 is a tough material with high resistance to abrasion and impact. It features good mechanical properties. By water absorption the excellent shock and vibration resistance is increased. Mechanical, electrical and dimensional properties are accordingly influenced by moisture absorption. These important characteristics add up to impressive cost / performance ratios. Typical applications for Zellamid® 202 are ball bearing races, friction bearings, pulleys, sheeves, gears, slipper blocks, vibration dampeners and absorbers, bowling pin setters, scrapers and many more.
Physical Properties Metric English Comments
Density 1.13 - 1.15 g/cc
0.0408 - 0.0415 lb/in³
Dry Density
Moisture Absorption at Equilibrium 2.6 - 3.4 %
2.6 - 3.4 %
Saturation at 50% RH; ISO 1110; DIN 53714
Water Absorption at Saturation 9.0 - 10 %
9.0 - 10 %
23°C; ISO 62; DIN 53495
Mechanical Properties Metric English Comments
Ball Indentation Hardness 70.0 MPa
10200 psi
H 358/30; ISO 2039; DIN 53456
Tensile Strength at Break 50.0 MPa
7250 psi
ISO 527; DIN 53455
Elongation at Break 200 %
200 %
ISO 527; DIN 53455
Tensile Modulus 1.50 GPa
218 ksi
ISO 527; DIN 53452
Charpy Impact, Notched NB
NB
double V-notch, rk=1.5 mm; DIN 53753
Tensile Creep Modulus, 1000 hours 230 MPa
33400 psi
23°C; ISO 899; DIN 53444
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 1218 Method A; DIN 53736
Maximum Service Temperature, Air 75.0 °C
167 °F
20,000 hours; 50% Tensile Strength; IEC 216; DIN 53446
90.0 °C
194 °F
5000 hours; 50% Tensile Strength; IEC 216; DIN 53446
<= 180 °C
<= 356 °F
a few hours operation
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Flame Spread <= 100 mm/min
<= 3.94 in/min
FMVSS - 302 flame propagation rate; DIN 75200
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 167; DIN 53482
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 167; DIN 53482
Dielectric Constant 7.0

@Frequency 1e+6 Hz
7.0

@Frequency 1e+6 Hz
IEC 250; DIN 53483
Dielectric Strength 60.0 kV/mm
1520 kV/in
IEC 243; VDE 0303T2
Dissipation Factor 0.30

@Frequency 1e+6 Hz
0.30

@Frequency 1e+6 Hz
IEC 250; DIN 53483
Comparative Tracking Index >= 600 V
>= 600 V
KB Method; IEC 112; DIN 53480
>= 600 V
>= 600 V
KC Method; IEC 112; VDE 0303T1
Descriptive Properties Value Comments
Time yield limit 5.5 MPa
23°C, s1/1000; ISO.899 DIN.53444