Zell-Metall Engineering Plastics Zellamid 250 GF 30 (PA6.6 + 30% glass fiber)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Zell-Metall Engineering Plastics
Trade Name Zellamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zell-Metall Engineering Plastics Zellamid 250 GF 30 (PA6.6 + 30% glass fiber).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zellamid® 250 GF 30 (PA 6.6 + 30% Glassfibre, black) is the registered trademark for Zell-Metall’s 30% glass fiber reinforced nylon grade 6.6. It offers increased strength, stiffness, creep resistance and dimensional stability whilst retaining good wear resistance. It also allows higher max. service temperatures.Fields: Transport and Conveyer Technology, Mechanical and Automotive Engineering, Precision Engineering, Processing Machinery.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
Moisture Absorption at Equilibrium 1.5 %
1.5 %
Saturation at 50% RH; ISO 1110; DIN 53714
Water Absorption at Saturation 5.5 %
5.5 %
23°C; ISO 62; DIN 53495
Mechanical Properties Metric English Comments
Ball Indentation Hardness 175 MPa
25400 psi
H 358/30; ISO 2039; DIN 53456
Tensile Strength at Break 160 MPa
23200 psi
ISO 527; DIN 53455
Elongation at Break 3.0 %
3.0 %
ISO 527; DIN 53455
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527; DIN 53452
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
double V-notch, rk=1.5 mm; DIN 53753
Thermal Properties Metric English Comments
CTE, linear 20.0 - 30.0 µm/m-°C

@Temperature 20.0 °C
11.1 - 16.7 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
DIN 52612
Thermal Conductivity 0.270 W/m-K
1.87 BTU-in/hr-ft²-°F
DIN 53612 Method A
Melting Point 255 °C
491 °F
ISO 1218 Method A; DIN 53736
Maximum Service Temperature, Air 200 °C
392 °F
a few hours operation
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75; DIN 53461
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75; DIN 53461
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in