Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Zell-Metall Engineering Plastics
Trade Name Zellamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oils, greases, most organic solvents and alkalis. Moisture absorption is lower than for Nylon 6.Typical applications are friction bearings, gears, cams and cam followers, guides, sleeves, valve seats and articles subjected to high loads and/or for high temperature.
Physical Properties Metric English Comments
Density 1.13 - 1.15 g/cc
0.0408 - 0.0415 lb/in³
Dry Density
Moisture Absorption at Equilibrium 2.5 - 3.1 %
2.5 - 3.1 %
Saturation at 50% RH; ISO 1110; DIN 53714
Water Absorption at Saturation 8.0 - 9.0 %
8.0 - 9.0 %
23°C; ISO 62; DIN 53495
Mechanical Properties Metric English Comments
Ball Indentation Hardness 100 MPa
14500 psi
H 358/30; ISO 2039; DIN 53456
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527; DIN 53455
Elongation at Break 150 %
150 %
ISO 527; DIN 53455
Tensile Modulus 1.60 GPa
232 ksi
ISO 527; DIN 53452
Charpy Impact, Notched NB
NB
double V-notch, rk=1.5 mm; DIN 53753
Tensile Creep Modulus, 1000 hours 400 MPa
58000 psi
23°C; ISO 899; DIN 53444
Thermal Properties Metric English Comments
Melting Point 255 °C
491 °F
ISO 1218 Method A; DIN 53736
Maximum Service Temperature, Air 80.0 °C
176 °F
20,000 hours; 50% Tensile Strength; IEC 216; DIN 53446
95.0 °C
203 °F
5000 hours; 50% Tensile Strength; IEC 216; DIN 53446
<= 200 °C
<= 392 °F
a few hours operation
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Flame Spread <= 100 mm/min
<= 3.94 in/min
FMVSS - 302 flame propagation rate; DIN 75200
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 167; DIN 53482
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 167; DIN 53482
Dielectric Constant 5.0

@Frequency 1e+6 Hz
5.0

@Frequency 1e+6 Hz
IEC 250; DIN 53483
Dielectric Strength 80.0 kV/mm
2030 kV/in
IEC 243; VDE 0303T2
Dissipation Factor 0.20

@Frequency 1e+6 Hz
0.20

@Frequency 1e+6 Hz
IEC 250; DIN 53483
Comparative Tracking Index >= 600 V
>= 600 V
KB Method; IEC 112; DIN 53480
>= 600 V
>= 600 V
KC Method; IEC 112; VDE 0303T1
Descriptive Properties Value Comments
Time yield limit 6 MPa
23°C, s1/1000; ISO.899 DIN.53444