Zircar Ceramics Z-500 Alumina-Silica Insulation

Category	Ceramic , Oxide , Aluminum Oxide , Silicon Oxide
Manufacturer	Zircar Ceramics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Ceramics Z-500 Alumina-Silica Insulation.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Useful to temperatures of 1000°C (1832°F) Z-500 is uniformly rigidized and hard throughout its entire thickness, requiring no re-rigidizing after precision machining into complex shapes and confiations.Information provided by Zircar Ceramics.

Physical Properties	Metric	English	Comments
Density	0.800 g/cc	0.0289 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	94	94	No Scale Listed
Modulus of Rupture	0.00530 GPa	0.769 ksi	Parallel to Thickness
Compressive Yield Strength	2.80 MPa	406 psi	at 2% Compression, Parallel to thickness
	6.27 MPa	910 psi	at 10% Compression, Parallel to Thickness

Thermal Properties	Metric	English	Comments
CTE, linear	3.70 µm/m-°C @Temperature 20.0 - 900 °C	2.06 µin/in-°F @Temperature 68.0 - 1650 °F	after initial firing
Maximum Service Temperature, Air	1000 °C	1830 °F
Shrinkage	0.700 % @Temperature 800 °C, Time 86400 sec	0.700 % @Temperature 1470 °F, Time 24.0 hour	Perpendicular to Thickness
	2.90 % @Temperature 1000 °C, Time 86400 sec	2.90 % @Temperature 1830 °F, Time 24.0 hour	Perpendicular to Thickness

Component Elements Properties	Metric	English
Al2O3	36 %	36 %
Fe2O3	0.30 %	0.30 %
SiO2	63 %	63 %
TiO2	0.70 %	0.70 %

Descriptive Properties	Value	Comments
Color	White