Zircar Refractory Composites RSLE-56 MOLDABLE Refractory Sheet
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Zircar Refractory Composites, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zircar Refractory Composites RSLE-56 MOLDABLE Refractory Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ZIRCAR Refractory Sheet Type RSLE-56 Moldable is a high silica fiber reinforced ceramic composite material that is easily cut and formed into flat sheets in addition to a wide variety of simple and complex shapes. When dried RSLE-56 Moldable becomes a hard rigid structure. Further heat treatment or exposure to process temperatures significantly increases the physical strength of this material.Information provided by ZIRCAR Refractory Composites, Inc. (ZRCI)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | |
| Solids Content | 73 % | 73 % | |
| Loss On Ignition | 2.0 % | 2.0 % | |
| Porosity | 36 % | 36 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 54 | 54 | dry |
| 70 | 70 | 10 hrs at 370°C | |
| 83 | 83 | 16 hrs at 1000°C | |
| Modulus of Rupture | 0.00758 GPa | 1.10 ksi | dry |
| 0.0159 GPa | 2.31 ksi | 10 hrs at 370°C | |
| 0.0262 GPa @Temperature 1000 °C, Time 57600 sec |
3.80 ksi @Temperature 1830 °F, Time 16.0 hour |
||
| Compressive Yield Strength | 49.6 MPa | 7190 psi | at 7% consolidation, 16 hrs at 1000°C |
| 11.7 MPa @Temperature 23.0 °C |
1700 psi @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.550 W/m-K @Temperature 200 °C |
3.82 BTU-in/hr-ft²-°F @Temperature 392 °F |
parallel to thickness; ASTM C1113 |
| 0.610 W/m-K @Temperature 600 °C |
4.23 BTU-in/hr-ft²-°F @Temperature 1110 °F |
parallel to thickness; ASTM C1113 | |
| 0.750 W/m-K @Temperature 1000 °C |
5.20 BTU-in/hr-ft²-°F @Temperature 1830 °F |
parallel to thickness; ASTM C1113 | |
| Shrinkage | 2.0 % | 2.0 % | linear |
| 3.0 % | 3.0 % | thickness |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Other | <= 1.0 % | <= 1.0 % | |
| SiO2 | 99 % | 99 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |