Zircar Zirconia ZR-CEM Zirconia Cement

Category Ceramic , Machinable Ceramic , Oxide , Zirconium Oxide
Manufacturer Zircar Zirconia
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zircar Zirconia ZR-CEM Zirconia Cement.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zircar Zirconia Cement Type ZR-CEM is an off white single part yttria-stabilized zirconia adhesive with a useful temperature limit of 2200°C. ZR CEM is formulated specifically for bonding Zircar Zirconia Felts, Boards and Cylinders to themselves or to back-up thermal insulations such as porous firebrick, alumina fiber and alumino-silicate fiber boards. ZRCEM is composed of yttria-stabilized zirconia milled fibers and sub-micron particles. Potassium silicate and zirconium acetate binders are added to enhance bonding characteristics. ZR-CEM will not bond to non-porous surfaces such as glass or steel. ZR-CEM is mildly acidic (pH 5.4) and forms a strong bond upon removal of the water solvent. For most furnace applications, the articles bonded together are ready for placing in service once the cement has dried. Curing at 426°C (800°F) or more may be desirable to eliminate the acetate prior to use. The cured bond joint is stronger than the tensile strength of 30 pound per cubic foot density Zircar Zirconia insulation material Types ZYFB-3, ZYZ-3 and ZYC. Pull out or de-lamination due to excessive mechanical or thermal stresses will usually first occur in the insulation material itself. ZR-CEM has the consistency of a thick paint and should be mixed thoroughly before using. ZR-CEM may be applied by dipping, brushing, or rolling. If ZR-CEM becomes thickened by evaporation, de-ionized or distilled water can be used to bring the cement back to its original consistency. ZR-CEM is non-flammable and is not affected by freezing. For a 0.01 inch thick bond, a pint of cement will cover about 7 square feet of joint surface.Features: High Temperature Stability to 2200°CWithstands Water and Steam after curingSafe to Use – Non-FlammableExcellent Thermal Shock ResistanceLow Shrinkage, High StrengthAvailable ‘Off the Shelf’Single Part SystemInformation provided by Zircar Zirconia.
Physical Properties Metric English Comments
Bulk Density 2.00 g/cc
0.0723 lb/in³
As supplied
3.10 g/cc
0.112 lb/in³
After drying
Solids Content 60 %
60 %
Viscosity 1200 cP

@Temperature 25.0 °C
1200 cP

@Temperature 77.0 °F
Thermal Properties Metric English Comments
Melting Point 2430 °C
4410 °F
Maximum Service Temperature, Air 2200 °C
3990 °F
Continuous
Component Elements Properties Metric English Comments
HfO2 1.0 - 2.0 %
1.0 - 2.0 %
K2O 1.2 %
1.2 %
SiO2 3.6 %
3.6 %
Y2O3 10 %
10 %
ZrO2 83 - 84 %
83 - 84 %
Descriptive Properties Value Comments
Trace Inorganics <0.3%
Weight Per Pint 953 grams