Zotefoams Plastazote® LD33LC Low Density Polyethylene Foam, Large Cell

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Zotefoams
Trade Name Plastazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® LD33LC Low Density Polyethylene Foam, Large Cell.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0270 - 0.0350 g/cc
0.000975 - 0.00126 lb/in³
sheet density
0.0330 g/cc
0.00119 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.900 - 1.60 mm
0.0354 - 0.0630 in
1.25 mm
0.0492 in
Typical Diameter
Mechanical Properties Metric English Comments
Hardness, Shore OO 53
53
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.365 MPa
52.9 psi
ISO 7214 1998
Elongation at Break 120 %
120 %
Compressive Yield Strength 0.0500 MPa

@Strain 10.0 %
7.25 psi

@Strain 10.0 %
BS ISO 7214 1998
0.0660 MPa

@Strain 25.0 %
9.57 psi

@Strain 25.0 %
BS ISO 7214 1998
0.0970 MPa

@Strain 40.0 %
14.1 psi

@Strain 40.0 %
BS ISO 7214 1998
0.131 MPa

@Strain 50.0 %
19.0 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 0.910 kN/m
5.19 pli
BS EN ISO 8067 1995
Compression Set 3.0 %

@Time 79200 sec,
Strain 25.0 %
3.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
9.5 %

@Time 79200 sec,
Strain 25.0 %
9.5 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
12.5 %

@Time 79200 sec,
Strain 50.0 %
12.5 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
22 %

@Time 79200 sec,
Strain 50.0 %
22 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0562 W/m-K
0.390 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 100 °C
212 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 1.0

@Thickness 13.0 mm
1.0

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
1.6

@Thickness 5.00 mm
1.6

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998