Zylog Neoplast® 180 HOFR Thermoplastic Vulcanizate

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer	Zylog Plastalloys
Trade Name	Neoplast®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zylog Neoplast® 180 HOFR Thermoplastic Vulcanizate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Neoplast 180 HOFR is a flame retardant thermoplastic vulcanizate (TPV) compound, based on polyolefin chemistry, suitable for Injection Molding and Extrusion applications.RoHS Compliant, UV StabilizedInformation provided by Zylog Plastalloys Pvt. Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	ASTM D 792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	90	90	ASTM D 2240
	92 @Time 605000 sec	92 @Time 168 hour	Heat Aging; ASTM D 2240/ASTM D 573
Tensile Strength, Ultimate	12.7 MPa	1850 psi	500 mm/min; ASTM D 412
	14.0 MPa @Time 605000 sec	2030 psi @Time 168 hour	Heat Aging; ASTM D 412/ASTM D 573
Elongation at Break	550 %	550 %	500 mm/min; ASTM D 412
	440 % @Time 605000 sec	440 % @Time 168 hour	Heat Aging; ASTM D 412/ASTM D 573
100% Modulus	0.00931 GPa	1.35 ksi	500 mm/min; ASTM D 412
Tear Strength	68.6 kN/m	392 pli	500 mm/min; ASTM D 624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	130 °C	266 °F	Continuous; SAE J 2236
Brittleness Temperature	-55.0 °C	-67.0 °F	ASTM D 746
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in
Oxygen Index	26 %	26 %	ASTM D 2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.00e+16 ohm-cm	3.00e+16 ohm-cm	ASTM D 257
Dielectric Constant	2.5	2.5	ASTM D 150
Dielectric Strength	30.0 kV/mm	762 kV/in	ASTM D 149