- Polymer Property : Linear Mold Shrinkage, Transverse = 0.0040 cm/cm
Polymer Property : Linear Mold Shrinkage, Transverse = 0.0040 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC
LNP* LUBRICOMP* DFL369XF is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Asia Pacific)
LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI (Asia Pacific)
LNP* Lubricomp* EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific)
LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0070
cm/cm @Time 86400 sec |
0.0040
-
0.0070
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK
LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear (Asia Pacific)
LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Easy Molding.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Lubricomp OFB32I PPS
LNP LUBRICOMP* OFB32I is a compound based on Polyphenylene Sulfide resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SA..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP OX97635 PPS
LNP LUBRICOMP* OX97635 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Wear Resistant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Asia Pacific)
LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing Silicone, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Europe-Africa-Middle East)
LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing Carbon Fiber, Silicone, PTFE. Added features of this material include: Electrically Conductive.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRILOY DF2041 PC
LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added features include: Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Europe-Africa-Middle East)
LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific)
40% GR, increased strength/stiffness vs unreinforced. Non-flame retardant. For appliance handles, spotlights, electric motors, pump housings etc.This data was supplied by SABIC-IP for the Asia Pacif..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC
LNP* STAT-KON* DEL339XF is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Electrically Conductive, Flame Retardant, Wear Resistant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 701 PBT (Asia Pacific)
35% glass/mineral alloy, excellent electrical performance to dielectric breakdown. Developed for automotive distributor caps.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 735 PBT
40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.This data was supplied by SABIC-IP for the Americas re..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 865 PBT+PET (Asia Pacific)
30% GR PBTP, UL94 V-0 rated. Non-blooming flame retardant. Improved surface appearance. Same application areas as for VALOX 855.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HR426 PBT (Asia Pacific)
AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI (Asia Pacific)
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by ..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0070
cm/cm @Thickness 0.750 - 2.30 mm |
0.0040
-
0.0070
in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
|
SABIC Innovative Plastics Xenoy® 6370 PBT+PC
30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON ZE004 MODIFIED POLYPHENYLENE (Asia Pacific)
LNP* Stat-kon* ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0050
cm/cm @Time 86400 sec |
0.0040
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC
LNP THERMOCOMP* DF004ER is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. Mold Release.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI (Asia Pacific)
LNP* Thermocomp* EF006ER is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Stat-kon DX96690 PC
LNP STAT-KON* DX96690 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the America..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 451E PBT
20% GR. Easy flow version of VALOX 451.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP AF002XXC ABS
LNP THERMOCOMP* AF002XXC is a compound based on ABS resin containing 10% Glass Fiber.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC
LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP VERTON RV00CES PA 66
LNP VERTON* RV00CES is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP VERTON RV00CESS PA 66 (Asia Pacific)
LNP VERTON* RV00CESS is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm @Time 86400 sec |
0.0040
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP VERTON RX06424 PA 66
LNP VERTON* RX06424 is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized, Structural
|
|||