- Polymer Property : Linear Mold Shrinkage, Transverse = 0.0060 cm/cm
Polymer Property : Linear Mold Shrinkage, Transverse = 0.0060 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC
LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC (Asia Pacific)
LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC
LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC
LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI
LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP EFL36XXC PEI
LNP* Lubricomp* EFL36XXC is a compound based on Polyetherimide containing 30% Glass Fiber, 155 PTFE. Characteristics of this grade are: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 420 PBT (Asia Pacific)
30% GR, excellent strength, stiffness and dimensional stability. High heat resistance. Appliance handles, spotlights, electric motors, connectors.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 553U PBT+PC
30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 732E PBT + PC + PET
30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 735 PBT (Asia Pacific)
40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 735 PBT+PET
40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON DX05474 PC
LNP* STAT-KON* DX05474 is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant, Mold ..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 830 PBT
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 830 PBT (Asia Pacific)
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 865 PBT+PET
30% GR PBTP, UL94 V-0 rated. Non-blooming flame retardant. Improved surface appearance. Same application areas as for VALOX 855.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HR426 PBT
AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by ..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON ZE004 PPO
LNP* STAT-KON* ZE004 is a compound based on PPO resin containing 20% Carbon Fiber. Added feature of this grade includes: Electrically Conductive.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-LOY AF306 ABS
LNP* STAT-LOY* AF306 is a compound based on ABS resin containing 30% Glass Fiber. Added feature of this material is: Antistatic.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC
LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI
LNP* Thermocomp* EF006ER is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0050
-
0.0060
cm/cm @Time 86400 sec |
0.0050
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK
LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific)
LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 420SE0U PBT (Asia Pacific)
UV-Stabilized version of 420SE0.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 430 PBT (Asia Pacific)
33 % glass reinforced, impact modified. Connectors, etc.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HX420HP PBT
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Thickness 1.50 - 3.20 mm |
0.0040
-
0.0060
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HX420HP PBT (Europe-Africa-Middle East)
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC (Asia Pacific)
LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC (Asia Pacific)
LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0060
cm/cm @Time 86400 sec |
0.0040
-
0.0060
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU
LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
|
|||