Polymer Property : Linear Mold Shrinkage = 0.011 in/in Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	STN EN ISO 294-4
Plastcom SLOVAMID® 6 GF 40 HI PA6 reinforced with glass fiber, improved impact strength PA 6 for injection molding, reinforced with 40% glass fiber, impact modified. Application: impacted moldings and moldings with higher strength applied in automotive, electrical, engineering and cons..
Linear Mold Shrinkage	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	Across Flow; ISO 2577
Polykemi AB POLYfill PPH K20020 D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB
Linear Mold Shrinkage	0.011 - 0.015 cm/cm	0.011 - 0.015 in/in	ASTM D955
Polymer Resources NY6-GP1-[color]-H General Purpose Nylon 6, Heat Stabilized General Purpose Nylon 6, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grade..
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	ASTM D955
Multibase Multi-Pro® 2003 TI Polypropylene Talc Filler, 20% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	ASTM D955
RheTech Products HP531-01UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black Applications: IP structural componentsAir ducts - distributionA/B/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Linear Mold Shrinkage	0.011 - 0.014 cm/cm	0.011 - 0.014 in/in	With Flow; ISO 2577
Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Linear Mold Shrinkage	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	Across Flow; ISO 2577
Polykemi AB POLYfill PPH BK901213 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Linear Mold Shrinkage	0.011 - 0.018 cm/cm	0.011 - 0.018 in/in
Lehmann & Voss LUVOCOMÂ® 1105-8432 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect..
Linear Mold Shrinkage	0.011 - 0.015 cm/cm	0.011 - 0.015 in/in
Lehmann & Voss LUVOCOMÂ® 3-8266 Polyamide 6, unreinforced Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduce..
Linear Mold Shrinkage	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	ASTM D955
Kolon KOLEFINÂ® KO133MT20 M/F Reinforced Polypropylene KOLEFINÂ® has excellent mechanical properties and its cost is lower than other engineering plastics. KOLEFINÂ® is widely used in the automotive industry and business applications.Good mechanica..
Linear Mold Shrinkage	0.011 cm/cm @Thickness 3.17 mm	0.011 in/in @Thickness 0.125 in
Shakespeare Isocorâ„¢ SVP6100 Nylon 610 Isocorâ„¢ 6100 is a medium viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption and greater dimensional stability. Isocorâ„¢ 6100 is also u..
Linear Mold Shrinkage	0.011 - 0.016 cm/cm @Thickness 3.20 mm	0.011 - 0.016 in/in @Thickness 0.126 in	48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	ASTM D955
Teknor Apex Telcar® TL-1000-92 Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Spec..
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	Borealis Method
Borealis Daplen™ MD206U Polypropylene Compound 20% Mineral Filled Daplen MD206U is a 20% mineral filled polypropylene compound intended for injection molding. MD206U has been developed especially for automotive interior parts that require excellent balance betwee..
Linear Mold Shrinkage	0.011 cm/cm @Thickness 3.175 mm	0.011 in/in @Thickness 0.1250 in	ASTM D955
A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66 Information provided by A. Schulman.
Linear Mold Shrinkage	0.011 cm/cm @Thickness 3.175 mm	0.011 in/in @Thickness 0.1250 in	ASTM D955
A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman.
Linear Mold Shrinkage	0.011 - 0.015 cm/cm @Thickness 3.20 mm	0.011 - 0.015 in/in @Thickness 0.126 in	72 hr; ISO 294
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i..
Linear Mold Shrinkage	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	GB/15585
Zhejiang Juner JEPP2056 PP For Automotive Parts Applications: BumpersInformation provided by Zhejiang Juner New Materials Co, Ltd.
Linear Mold Shrinkage	0.011 cm/cm @Thickness 2.00 mm	0.011 in/in @Thickness 0.0787 in
Toyobo PELPRENE™ P90BD Polyester TPE, High Viscous, High Durability Features: Polyester TPE, High Viscous, High DurabilityInformation provided by Toyobo.
Linear Mold Shrinkage	0.011 - 0.019 cm/cm @Thickness 3.20 mm	0.011 - 0.019 in/in @Thickness 0.126 in	72 hr; ISO 294
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Linear Mold Shrinkage	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in
A. Schulman POLYTROPE™ TPP 510 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 510 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi..
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in
E-Polymers SEPAZ® V230B 30% Mineral Filled Reinforced PPA Polyphthal Amide Resin (High Temperature Nylon): SEPAZ PPA is a unique semi-crystalline engineering plastic that bridges the cost-performance gap between traditional engineering thermoplastics and s..
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	ASTM D955
Buckeye Polymers BP RPP 1510 C Polypropylene, 15% Mineral Filled Calcium carbonate-filled PP grades have a high impact toughness, moderate increased stiffness, and excel in high gloss applications. This material can be customized through the addition of UV packag..
Linear Mold Shrinkage	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	Across Flow; ISO 2577
Polykemi AB POLYfill PPH TS3020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	Borealis Method; average process
Borealis MD231U Polypropylene Compound, Mineral Filled MD231U is a 20 % mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and a medium melt flow rate. Applications: Air duc..
Linear Mold Shrinkage	0.011 - 0.014 cm/cm	0.011 - 0.014 in/in	after bake; ISO 294
Solvay Engineered Polymers DEXFLEX® 880-1 TPO  (discontinued **) Description: DEXFLEX® 880-1 is a thermoplastic olefinic elastomer (TPO) designed for exterior automotive applications requiring a combination of stiffness, low-temperature impact, good processabili..
Linear Mold Shrinkage	0.011 - 0.015 cm/cm	0.011 - 0.015 in/in	ISO 2577
Polyram RamOfin PPH343T4BK11 Polypropylene, 20% Mineral Filled 20% Mineral filled, UV stabilized, heat resistant polypropylene for injection molding applications.Information provided by Polyram.
Linear Mold Shrinkage	0.011 - 0.016 cm/cm	0.011 - 0.016 in/in
Lehmann & Voss LUVOCOM® 1-8228 Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..