- Polymer Property : Linear Mold Shrinkage, Flow = 0.0025 cm/cm
Polymer Property : Linear Mold Shrinkage, Flow = 0.0025 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm | 0.0020 - 0.0025 in/in | ASTM D955 |
|
PolyOne LubriOne™ SF-30GF/15T Polyphenylene Sulfide (PPS)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
|
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | ISO 294-4 |
|
Polyplastic Armamid® PA GF25-1FR Nylon 6, 25% Glass Fiber
Flame retardant, RoHS compliantInformation provided by PolyPlastic Group.
|
|||
| Linear Mold Shrinkage, Flow |
0.00050
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.00050
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics Lexan® LGK3020 PC (Asia Pacific)
Glass reinforced. Flame retardant.
|
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | on tensile bar; SABIC Method |
|
SABIC Innovative Plastics LNP Lubricomp DEL34 PC (Europe-Africa-Middle East)
LNP* Lubricomp* DEL34 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP f..
|
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | |
|
LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced
Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplasti..
|
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | |
|
LATI Latigloss 57 G/60 F2 PPA, 60% Glass Fiber Reinforced
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact application. Availability: ..
|
|||
| Linear Mold Shrinkage, Flow |
0.0020
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0020
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East)
Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod..
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC (Asia Pacific)
20% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
|
|||
| Linear Mold Shrinkage, Flow |
0.00050
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.00050
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC (Europe-Africa-Middle East)
LNP* Lubricomp* Lexan_FL1530 compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+HIPS (Europe-Africa-Middle East)
LNP* Lubricomp* Noryl_NF1520 compound is a 20% glass reinforced, 15% PTFE. Wear resistant; 211F HDT @ 264 psi.
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics Ultem 3451 PEI
45% Glass fiber and mineral filled, standard flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | on tensile bar; SABIC Method |
|
SABIC Innovative Plastics LNP Stat-kon DCL33 PC (Europe-Africa-Middle East)
LNP* Stat-kon* DCL4033 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP ..
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+HIPS (Europe-Africa-Middle East)
LNP* Stat-kon* Noryl_FMC3008A compound is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated. Property values at 20% weight reduction, 0.250"" wall.
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+PS
LNP* Stat-kon* Noryl_FMC3008A compound is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated. Property values at 20% weight reduction, 0.250"" wall.
|
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | on Tensile Bar; SABIC Method |
|
SABIC Innovative Plastics LNP STAT-KON OE008A PPS - Branched (Europe-Africa-Middle East)
LNP* Stat-kon* OC-1008 is a compound based on PPS - Branched resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics Xenoy® X2420 PC+POLYESTER (Asia Pacific)
Xenoy*X2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad co..
|
|||
| Linear Mold Shrinkage, Flow |
0.0010
-
0.0025
cm/cm <br>@Time 86400 sec
|
0.0010
-
0.0025
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific)
LNP* Thermocomp* D451 (or EXTC8141) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good duc..
|
|||
| Linear Mold Shrinkage, Flow |
0.0010
-
0.0025
cm/cm <br>@Time 86400 sec
|
0.0010
-
0.0025
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF00A1P PC (Asia Pacific)
LNP* Thermocomp* DF00AIP is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, low warpage, Non-Brominated & Non..
|
|||
| Linear Mold Shrinkage, Flow |
0.0010
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0010
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS (Asia Pacific)
10% GR, ECO conforming FR, PC+ABS for thinwall molding applications.
|
|||
| Linear Mold Shrinkage, Flow |
0.00050
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.00050
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East)
LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced, flame retardant material.
|
|||
| Linear Mold Shrinkage, Flow |
0.00050
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.00050
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC
LNP* Thermocomp* Lexan_LGN5030 compound is a glass reinforced. Flame retardant.
|
|||
| Linear Mold Shrinkage, Flow |
0.00050
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.00050
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC (Europe-Africa-Middle East)
LNP* Thermocomp* Lexan_LGK5020 compound is a glass reinforced, flame retardant material.
|
|||
| Linear Mold Shrinkage, Flow |
0.0020
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0020
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Asia Pacific)
Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio..
|
|||
| Linear Mold Shrinkage, Flow |
0.0010
-
0.0025
cm/cm <br>@Time 86400 sec
|
0.0010
-
0.0025
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP D452 PC COPOLYMER (Asia Pacific)
LNP* Thermocomp* D452 (or EXTC8202) is a compound based on SABIC unique Polycarbonate copolymer resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, ..
|
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | on tensile bar; SABIC Method |
|
SABIC Innovative Plastics LNP Thermocomp RF00AES PA 66 (Europe-Africa-Middle East)
LNP THERMOCOMP* RF00AES is a compound based on PA66 resin containing Glass Fiber, Mold Release.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics NORYL CN5258 PPE+PS (Asia Pacific)
40% filled FR high modulus PPE/PS blend
|
|||
| Linear Mold Shrinkage, Flow |
0.0020
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0020
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Asia Pacific)
Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus ..
|
|||
| Linear Mold Shrinkage, Flow |
0.0020
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0020
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East)
Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod..
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+HIPS (Europe-Africa-Middle East)
LNP* Stat-kon* Noryl_FMC1010 compound is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94 V1 rated. Property values at 20% WR, 0.250"" wall.
|
|||
| Linear Mold Shrinkage, Flow |
0.0015
-
0.0025
cm/cm <br>@Thickness 3.20 mm
|
0.0015
-
0.0025
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics NORYL CN5260 PPE+PS (Asia Pacific)
50% filled FR high modulus PPE/PS blend
|
|||