- Polymer Property : Linear Mold Shrinkage, Transverse = 0.0030 in/in
Polymer Property : Linear Mold Shrinkage, Transverse = 0.0030 in/in Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0080
cm/cm <br>@Thickness 3.17 mm
|
0.0030
-
0.0080
in/in <br>@Thickness 0.125 in
|
ASTM D955 |
|
Network Polymers Softflex® 7000
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Thickness 3.20 mm
|
0.0030
-
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics Cycoloy® C4210HF PC+ABS
PC+ABS Blend with 10% Glass Reinforce. High flow, High heat resistance., Excellent balance strength/rigidity. Good impact/appearance.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | Euronil |
|
Nilit Nilamid A3 H G10 50% Glass Reinforced PA66
Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance,..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Thickness 3.20 mm
|
0.0030
-
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C2801 PC+ABS (Asia Pacific)
5% PTFE reinforced PC+ABS wear resistant flame retardant resin for moving components in business equipment. Medium heat performance
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
|
LNP Stat-Kon® EC-1008 EM BK8-115 Polyetherimide, Carbon Fiber Reinforcement
(discontinued **)
Features: Electrically Conductive, Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; howev..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D995 |
|
Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced
Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D995 |
|
Kotec Carbotex KG-30MRA Polycarbonate, 30% Glass Fiber Reinforced
Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
|
LATI Larpeek 50 K/30 PEEK, 30% Carbon Fiber Reinforced
Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Thickness 3.20 mm
|
0.0030
-
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics ULTEM 2410EPR PEI
40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Thickness 3.20 mm
|
0.0030
-
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics ULTEM 3452 PEI (Asia Pacific)
45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Thickness 3.20 mm
|
0.0030
-
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE
50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Time 86400 sec
|
0.0030
-
0.0050
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON AX02747 ABS
LNP* STAT-KON* AX02747 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0045
cm/cm <br>@Time 86400 sec
|
0.0030
-
0.0045
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON EX03319C PEI (Asia Pacific)
LNP* Stat-Kon* EX03319C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding applicati..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Time 86400 sec
|
0.0030
-
0.0050
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC
LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features include: Exceptional Processing, Non-Brominated & Non-Chlorinated Flame Retardant.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0060
cm/cm <br>@Time 86400 sec
|
0.0030
-
0.0060
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DX09402 PC
LNP* THERMOCOMP* DX09402 is a compound based on Polycarbonate containing Proprietary Filler(s).
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Time 86400 sec
|
0.0030
-
0.0050
in/in <br>@Time 24.0 hour
|
ASTM D 955 |
|
SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear
LNP* Thermocomp* OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
|
Shinkong Synthetic Fibers Shinite® F102G30 PET, 30% Glass Filled, Fire Retardant, Halogen Free
Information from Shinkong Synthetic Fibers Corp.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Time 86400 sec
|
0.0030
-
0.0050
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON DEL359EF PC
LNP* STAT-KON* DEL359EF is a compound based on Polycarbonate containing 25% Carbon Fiber, 15% PTFE. Added features include: Flame Retardant. Electrically Conductive, Wear Resistant.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
|
Shinkong Synthetic Fibers Shinite® F102G30 PET, 30% Glass Filled, Fire Retardant, Halogen Free
Information from Shinkong Synthetic Fibers Corp.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
|
EMS-Grivory Grivory® BGZ-50/2 PA6-I-GF50
Information provided by EMS Grivory
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
|
EMS-Grivory Grivory® GV-6 FWA black 9225 PA*-GF60
Product description: Grivory GV-6 FWA black 9225 is a 60% glass-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline Polyamide with partially aromatic copol..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
|
EMS-Grivory Grivory® GV-6 FWA nat PA*-GF60
Product description: Grivory GV-6 FWA natural is a 60% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copolyami..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
|
EMS-Grivory Grivory® XE 4116 nat PA1010-GF55
Product description: Grilamid XE 4116 natural is a 55% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is especially suitable for the manufacturing of thin-walled, painted ..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
|
EMS-Grivory Grivory® LC-3H black PA12-CF30
Product description: Grilamid LC-3H BLACK is a Polyamide 12 injection molding product reinforced with 30 % carbon fibers. The product is inherently black and is only available in this color.Main Att..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
|
EMS-Grivory Grivory® GV-6H EF nat PA*-GF60
Product description: Grivory GV-6H EF black 9915 is a 60% glass-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline Polyamide with partially aromatic copol..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
|
LNP Lubricomp® JFL-4036 Polyethersulfone, Glass Fiber Reinforcement, PTFE Lubricant
(discontinued **)
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0030
-
0.0050
cm/cm <br>@Thickness 3.20 mm
|
0.0030
-
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
|
SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Asia Pacific)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Asia Pacif..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
|
LATI Latimass 62-01 D025 PA6
Specific density compound based on Polyamide 6 (PA6). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Ter..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
|
E-Polymers SEPAZ® K365GM 60% Glass Fiber/Calcium Carbonate Reinforced General Purpose PPS Resin
Polyphenylene Sulfide Resin: High-performance engineering plastic SEPAZ PPS boasts excellent high-temperature resistance, flame retardancy and chemical resistance, physical strength, and its fluidit..
|
|||