Polymer Property : Melt Flow = 1.3 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Melt Flow	1.3 g/10 min @Load 3.80 kg, Temperature 230 °C	1.3 g/10 min @Load 8.38 lb, Temperature 446 °F
Polycasa Acryl® KR 2007/1 Acrylic Medium stiffness impact grade with good heat distortion resistance. Can be extruded to thin tubes and profile and film. Easy to vacuum form. Lamp covers, cable boxes.Data was collected by ISO met..
Melt Flow	1.3 g/10 min @Temperature 190 °C	1.3 g/10 min @Temperature 374 °F
North Wood Plastics 60 PP + UNIFILL (20% Wood Fiber) Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It..
Melt Flow	1.3 g/10 min	1.3 g/10 min	Condition E; ASTM D 1238
Chevron Phillips 5554-D LDPE High Clarity, Medium Impact, Low Slip Film Resin  (discontinued **) Resin Type: HomopolymerCharacteristics: Excellent Clarity, Good Impact Strength, Good Sealability, Low SlipApplications:Food Packaging, Case Shrink Wrap, LaminationsProcessing Conditions: Extruder 6..
Melt Flow	1.3 g/10 min	1.3 g/10 min	Condition E; ASTM D 1238
Chevron Phillips 5554-H LDPE High Clarity, Medium Impact Film Resin  (discontinued **) Resin Type: HomopolymerCharacteristics: Excellent Clarity, Good Impact Strength, Excellent Processability, Low Coefficient of Friction, Good SealabilityApplications:Bread Bag, Dry Goods Packaging, P..
Melt Flow	1.3 g/10 min	1.3 g/10 min	Condition E; ASTM D 1238
Eastman 5251 LDPE 4% VA Copolymer, High Clarity, High Impact Film Resin for Laminations  (discontinued **) Resin Type: VA CopolymerCharacteristics: Excellent adhesion, Excellent processability and bubble stability, High slip and antiblock, Good impact strengthApplications:Laminations, Heavy produce and s..
Melt Flow	1.3 g/10 min	1.3 g/10 min	Exxon Method
ExxonMobil Escorene® LD-302 EVA Film Resin, High Clarity, High Impact  (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.4% vinyl acetate copolymer, high clarity film resin. The combination of low melt index and comonomer content helps produce films which exhibit ..
Melt Flow	1.3 g/10 min	1.3 g/10 min	Exxon Method
ExxonMobil Escorene® LD-325 EVA Film Resin, High Clarity, High Impact  (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.8% vinyl acetate copolymer, high clarity film resin. The combination of low melt index and comonomer content helps produce films which exhibit ..
Melt Flow	1.3 g/10 min	1.3 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA814000 Low Density Polyethylene ApplicationsPETROTHENE NA 814-000 is a low density homopolymer resin specifically developed for a wide variety of blow molding applications. This resin exhibits excellent gloss, an excellent balanc..
Melt Flow	1.3 g/10 min	1.3 g/10 min	ISO 1133
Solvay Specialty Polymers PolidanÂ® TUX 100 Polyethylene, Crosslinked (XLPE) PolidanÂ® TUX 100 is a high density crosslinkable polyethylene compound manufactured according to the SioplasÂ® process. It has been developed for the production of crosslinked pipes in a wide r..
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 190 Â°C	1.3 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Solvay Specialty Polymers PolidiemmeÂ® G/420 Thermoset Elastomer (TSE) PolidiemmeÂ® XLPO -Cross-linkable Polyolefin. Elastomer based compound crosslinkable by ambient moisture, consisting of a silane pregrafted base compound to be used with a catalyst masterbatch (Si..
Melt Flow	1.3 g/10 min	1.3 g/10 min	ASTM D1238
Shuman 210 Polyphenylene Ether Copolymer Alloy Black, Custom Colors. Good impact strength, easy processability, good chemical resistance, injection molding and extrusion grades.Data provided by the manufacturer.
Melt Flow	1.3 g/10 min @Load 10.0 kg, Temperature 190 Â°C	1.3 g/10 min @Load 22.0 lb, Temperature 374 Â°F	EVA/ATH/NanofilÂ® 5 (42:55:3)
SÃ¼d-Chemie NanofilÂ® 5 Flame Retardant Standard grades for inorganic flame retardant cable formulations with good pre-dispersibility.Application:PE/EVAGrafted PP Cable formulationAutomotiveTechnical PartsImproves: Abrasion/Scratch Resist..
Melt Flow	1.3 g/10 min @Load 5.00 kg, Temperature 280 Â°C	1.3 g/10 min @Load 11.0 lb, Temperature 536 Â°F	ASTM D1238
SABIC Innovative Plastics NORYL HH180 PPE+PS Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365.
Melt Flow	1.3 g/10 min @Load 5.00 kg, Temperature 280 Â°C	1.3 g/10 min @Load 11.0 lb, Temperature 536 Â°F	ASTM D1238
SABIC Innovative Plastics NORYL HH180 PPE+PS (Asia Pacific) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365.
Melt Flow	1.3 g/10 min @Load 5.00 kg, Temperature 260 Â°C	1.3 g/10 min @Load 11.0 lb, Temperature 500 Â°F	ASTM D1238
SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP 40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 190 °C	1.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
DuPont Nucrel® 31001 Ethylene-Acrylic Acid Copolymer Resin for Blown and Cast Film 9.5 wt% Acrylic Acid.Nucrel® 31001 is an ethylene-acrylic acid copolymer resin available for use in blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins.F..
Melt Flow	1.3 g/10 min	1.3 g/10 min	Condition E; ASTM D 1238
Chevron Phillips MarFlex® 5563 LDPE High Clarity, Medium Impact Film Resin Resin Type: HomopolymerCharacteristics: Good Optics, Good Impact Strength, Excellent Processability, Good Heat Seal Characteristics, High Slip, High AntiblockApplications:Bakery Film, Soft Goods, Pr..
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 190 °C	1.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
DuPont™ Surlyn® 1601-2 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 1601-2 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, s..
Melt Flow	1.3 g/10 min	1.3 g/10 min	ExxonMobil Method
ExxonMobil LD 302.56 High Clarity, High Impact Film Resin LD 302 Series films exhibit superior impact strength, good heat sealability, and good low temperature properties. Typical applications are frozen food packaging or other food packaging.Information ..
Melt Flow	1.3 g/10 min @Load 3.80 kg, Temperature 230 °C	1.3 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238
Diamond Polymers ABS 9950 Injection Molding Grade Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	1.3 g/10 min @Load 5.00 kg, Temperature 200 °C	1.3 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Diamond Polymers ABSPC 8020 Very High Impact Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	1.3 g/10 min @Load 5.00 kg, Temperature 200 °C	1.3 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Diamond Polymers NPP 808 C4 TDS Polycarbonate Alloy Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	1.3 g/10 min	1.3 g/10 min	ASTM D1238
Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact Information provided by Asahi Thermofil
Melt Flow	1.3 g/10 min @Load 3.80 kg, Temperature 230 °C	1.3 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238
Arkema Group Solarkote® P-600 Acrylic PVC Capstock, clear, high glossInformation provided by Arkema Group
Melt Flow	1.3 g/10 min	1.3 g/10 min	ASTM D1238
Total PPC 4280W Polypropylene, Impact Copolymer ATOFINA 4280W polypropylene is a nucleated impact copolymer. 4280W has a low fluidity providing melt strength with excellent impact properties. It is nucleated for added stiffness and surface hard..
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 190 °C	1.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil LDPE LD 302.32 Low Density Polyethylene Resin Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact stren..
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 230 °C	1.3 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Braskem F013M Homopolymer Polypropylene Description: General PurposeApplications: Suggested Uses Include Strapping, ProfilesThis resin meets the requirements for olefin polymers as defined in 21 CFR, section 177.1520 issued by the Food an..