- Polymer Property : Melt Flow = 3.6 g/10 min
Polymer Property : Melt Flow = 3.6 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 275 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
|
PolyOne LubriOne™ NN-30CF/15T-02S black Polyamide 66 (Nylon 66)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
|
PolyOne Maxxam™ SY 89-23-7 Polypropylene, Unspecified (PP, Unspecified)
Maxxam ™ SY 89-23-7 is a polypropylene copolymer compound with a pre-dispersed blowing agent for up to 60% expansion. The compound offers consistent cell structure, dielectric properties, and stren..
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
|
SABIC 324CN Linear Low Density Polyethylene for Wire & Cable
Product Description: 324CN is a Linear Low Density Polyethylene natural resin for wire and cable applications. It contains a low level of antioxidants and does not contain any slip or antiblock a..
|
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | Condition 230/2-8; ASTM D1238 |
|
Plaskolite West Optix® CA-75 General Purpose Acrylic Resin
Injection Molding and Extrusion Grade Pellets. Highest heat resistance, medium flow.
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
|
Polimeri Europa Clearflex® CM 406 Hexene Copolymer Linear Low Density Polyethylene
Clearflex CM 406 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CM 406 are characterized by h..
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Data |
|
Americas Styrenics Styron® 8100 MFD High Impact Polystyrene
(discontinued **)
STYRON 8100 MFD high impact polystyrene is designed for microfloppy diskettes (MFD) applications. It offers easy processing, coloring, abrasion resistance, impact strength, and high heat resistance...
|
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | Exxon Method |
|
ExxonMobil Escorene® LD-401 EVA for Electrical Insulation
(discontinued **)
Data provided by the manufacturer, Exxon Chemical.A crosslinkable, 9.9% vinyl acetate copolymer designed for electrical applications.Applications: Base resin for fully formulated low voltage cable i..
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
|
Ineos Styrenics 166H General Purpose Polystyrene (NAFTA)
Description: Polystyrene 166H is a high molecular weight general purpose polystyrene with good flow and crystal clarity. Polystyrene 166H offers good processing characteristics while yielding parts ..
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
|
Ineos Styrenics Avantra® 525K High Impact Styrenic Polymer (NAFTA)
Description: Specialty and super-high impact grades for a variety of applications such as refrigerator liners, consumer electronics housings, recreation equipment and sporting goods, toys, office pr..
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
|
Ineos Styrenics Avantra® 585K Rubber Modified Polystyrene
Avantra® 585K is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical impact strength. Although Avantra® 585K can be processed by any method applicable..
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
|
Iran Petrochemical (PCC) 6040UA High Density Polyethylene
HD-6040UA is an ultra-violet light stabilized high density polyethylene injection grade with a narrow molecular weight distribution, specially developed for injection molding of heavy duty parts for..
|
|||
| Melt Flow |
3.6
g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6
g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
|
Mitsubishi Xantar® 27 R Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
|
|||
| Melt Flow |
3.6
g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6
g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
|
Mitsubishi Xantar® 27 SR FD Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
|
|||
| Melt Flow |
3.6
g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6
g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
|
Mitsubishi Xantar® 27 U Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
|
|||
| Melt Flow |
3.6
g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6
g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
|
Mitsubishi Xantar® MX 1071 FD Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
|
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | ASTM D1238G |
|
Hannam Chemical Hanalac 711 ABS, Plating Grade
Plating grade with excellent moldability and easy to surface treat. It also has a strong adhesive strength after plating and an excellent heat cycle. Applications: Appliances, TV frames, automoti..
|
|||
| Melt Flow | 3.6 - 10 g/10 min | 3.6 - 10 g/10 min | |
|
Shandong Dongyue Shenzhou New Material Co DS603B Fluorinated Ethylene Propylene Dispersion (DS603A/B)
Conformable with: Q/DYS 004-2007Fluorinated Ethylene Propylene concentrated dispersion is the copolymer of TFE and HFP, stabilized with non-ionic surfactant. It endow FEP products which can't be pr..
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
|
Samsung Cheil Industries Starex® VE-0857 ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
|
Styrolution PS 7800 HIPS
Extremely high surface glossGood processabilityUL Classification 94 HBInformation provided by Styrolution
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 177 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 351 °F |
ASTM D1238 |
|
Teknor Apex Flexalloy® 9800-60 Polyvinyl Chloride Elastomer
Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Oil Resistant, Ultra High MWUses- Footwear, Tubing, Gaskets, Tools (Power/Others), Hose, Wire and ..
|
|||
| Melt Flow |
3.6
g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6
g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
|
Styrolution PS 2610 GPPS
Extruded packaging; Thermoforming applicationsExcellent toughnessHigh melt strengthGood flow and processabilityInformation provided by Styrolution
|
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | |
|
UBE UBEPOL BR13HB HIPS (n-DM =0.03 wt %)
Description: UBEPOL-BR13HB is characterized by its low solution viscosity compared with conventional grades and short dissolution time in styrene monomer. Its main merits are as follows:Short dissol..
|
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | |
|
UBE UBEPOL BR15HB HIPS (n-DM =0.03 wt %)
Description: UBEPOL-BR15HB is characterized by the highest branching of these 3 grades and is adapted by many PS manufacturers.Information provided by UBE.
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 235 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
|
UBE UBESTA® 3030JI5L Plasticized Automotive Grade Nylon 12
Description: UBE UBESTA® Automotive grade Nylon 12Comments: meet SAE J844, DIN73378 HIPHLInformation provided by UBE.
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 235 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
|
UBE UBESTA® 3030JI7 Plasticized Industrial Grade Nylon 12
Description: UBE UBESTA® Industrial grade Nylon 12Comments: low migrationInformation provided by UBE.
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
|
ExxonMobil LLDPE LL 1236.85 Linear Low Density Polyethylene Resin
Product Description: LL 1236 Series resins are butane LLDPEs with increased stiffness and a high melt index. They can be used alone or as a component in packaging and industrial film, blown or cast...
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
|
ExxonMobil LLDPE LL 1236.86 Linear Low Density Polyethylene Resin
Product Description: LL 1236 Series resins are butane LLDPEs with increased stiffness and a high melt index. They can be used alone or as a component in packaging and industrial film, blown or cast...
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 374 °F |
ExxonMobil Method |
|
ExxonMobil Vistamaxx™ 3000 Propylene-based Elastomer
Product Description: Vistamaxx 3000 propylene-based elastomer is an olefinic elastomer produced using ExxonMobil Chemical's EXXPOL™ Technology. It has moderate elastomeric properties, is easy to ..
|
|||
| Melt Flow |
3.6
g/10 min @Load 2.16 kg, Temperature 230 °C |
3.6
g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
|
Braskem D036W6 Homopolymer Polypropylene
Description: Injection Molding, General Purpose, Low Water CarryoverApplications: Suggested Uses Include Tape, Slit-film Fibers, Containers, Closures, HousewaresThis resin meets the requirements for..
|
|||
| Melt Flow |
3.6
g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6
g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
|
Mitsubishi Xantar® 27 UR Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher..
|
|||