Polymer Property : Melt Flow = 8.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Melt Flow	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE G 7890 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow	4.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C	4.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F	STN EN ISO 1133
Plastcom PLASTALEN® EH 91 N Polyethylene HDPE regrind for injection molding. General use in all industry branches. Delivered in blue ( approx. RAL 5015) mode.Information Provided by Plastcom spol. s r.o.
Melt Flow	6.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C	6.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F	ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 8300M (EPC30R) Propylene and Ethylene Block Polymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow	1.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 265 °C	1.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 509 °F	ASTM D1238
Polymer Resources PC/TP-GP3-G20 PC/Polyester Alloy, 20% Glass Reinforced Superior Chemical Resistance, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Melt Flow	1.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 265 °C	1.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 509 °F	ASTM D1238
Polymer Resources PC/TP-GP3-G30 PC/Polyester Alloy, 30% Glass Reinforced Superior Chemical Resistance, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Melt Flow	4.0 - 8.0 g/10 min <br>@Load 11.6 kg,<br> Temperature 250 °C	4.0 - 8.0 g/10 min <br>@Load 25.6 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources PPX-EN-FR3 Modified-PPO, V-1 Flame Retardant, Extrusion Grade Modified-Polyphenylene Oxide, V-1 Flame Retardant, 265F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducte..
Melt Flow	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
Polymer Resources PPX-FR3-[color]EN Modified PPO, UL 94 V-1 with HDT of 265 F, Extrusion Grade Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow	4.0 - 8.0 g/10 min <br>@Load 11.6 kg,<br> Temperature 250 °C	4.0 - 8.0 g/10 min <br>@Load 25.6 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources PPX-FR7 Modified-PPO, V-0 Flame Retardant Modified-Polyphenylene Oxide, V-0 Flame Retardant, 260F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor..
Melt Flow	1.0 - 8.0 g/10 min <br>@Load 11.6 kg,<br> Temperature 250 °C	1.0 - 8.0 g/10 min <br>@Load 25.6 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources PPX-G10 Modified-PPO, 10% Glass Reinforced Modified-Polyphenylene Oxide, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Melt Flow	1.0 - 8.0 g/10 min <br>@Load 11.6 kg,<br> Temperature 250 °C	1.0 - 8.0 g/10 min <br>@Load 25.6 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources PPX-G15 Modified-PPO, 15% Glass Reinforced, High Flow Modified-Polyphenylene Oxide, 10% Glass Reinforced, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf..
Melt Flow	1.0 - 8.0 g/10 min <br>@Load 11.6 kg,<br> Temperature 250 °C	1.0 - 8.0 g/10 min <br>@Load 25.6 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources PPX-G20 Modified-PPO, 20% Glass Reinforced Modified-Polyphenylene Oxide, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Melt Flow	2.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C	2.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources TP-FRHG15 Polybutylene Terephthalate, 15% Glass Reinforced Alloy, Flame Retardant Polybutylene Terephthalate, 15% Glass Reinforced Alloy, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test s..
Melt Flow	2.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C	2.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources TP-GFMF1 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced, Flame Retardant Polybutylene Terephthalate, 40% Glass/Mineral Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test..
Melt Flow	2.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C	2.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F	ASTM D1238
Polymer Resources TP-IM1 Polybutylene Terephthalate, Low Temperature Impact Modified Polybutylene Terephthalate, Low Temperature Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor..
Melt Flow	5.0 - 8.0 g/10 min	5.0 - 8.0 g/10 min	on the basis of basic grades 11503-070 and 16803-070
Kazanorgsintez P2KP Polyethylene Pigment Masterbatches Production Method: P2KP polyethylene pigment masterbatches are produced on the basis of low density polyethylene with high content of masterbatches. Application: P2KP polyethylene pigment masterbatc..
Melt Flow	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	ASTM D1238
Micropol L7 Low density polyethylene rotational molding powder Has a high gloss finish, and outstanding toughness. Information provided by Micropol Limited
Melt Flow	5.0 - 8.0 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 Â°C	5.0 - 8.0 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 Â°F	ASTM D1238
Lavergne VYSTYRENE PS 3901 High Impact Polystyrene Vystyrene PS 3901 is a black impact modified polystyrene compound with balanced impact/stiffness properties designed for injection molding applicationsFeatures: -High resilience -Excellent process..
Melt Flow	4.0 - 8.0 g/10 min <br>@Load 5.00 kg,<br> Temperature 372 Â°C	4.0 - 8.0 g/10 min <br>@Load 11.0 lb,<br> Temperature 702 Â°F	ASTM D1238
Solvay Specialty Polymers HyflonÂ® MFAÂ® F1530 Perfluoropolymer HyflonÂ® MFA is a family of perfluoro polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistanc..
Melt Flow	6.0 - 8.0 g/10 min <br>@Temperature 230 °C	6.0 - 8.0 g/10 min <br>@Temperature 446 °F	ASTM D1238
A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman.
Melt Flow	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene Information provided by A. Schulman.
Melt Flow	6.0 - 8.0 g/10 min <br>@Temperature 230 °C	6.0 - 8.0 g/10 min <br>@Temperature 446 °F	ASTM D1238
A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman.
Melt Flow	6.0 - 8.0 g/10 min <br>@Temperature 230 °C	6.0 - 8.0 g/10 min <br>@Temperature 446 °F	ASTM D1238
A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman.
Melt Flow	6.0 - 8.0 g/10 min <br>@Temperature 230 °C	6.0 - 8.0 g/10 min <br>@Temperature 446 °F	ASTM D1238
A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman.
Melt Flow	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene Information provided by A. Schulman.
Melt Flow	2.0 - 8.0 g/10 min	2.0 - 8.0 g/10 min
Daikin NEOFLON RP-5000AS EFEP Pellets NEOFLON EFEP is an ETFE based fluoropolymer combining the excellent physical properties derived from ETFE together with a low processing temperature that is more compatible with conventional thermop..
Melt Flow	6.0 - 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C	6.0 - 8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F	ASTM D1238
Arkema Group Orevac® 9318 Film EVA-MAH Terpolymer EVA Terpolymers based Main Applications: Extrusion coating Thermo-adhesive filmsInformation provided by Arkema Group
Melt Flow	3.0 - 8.0 g/10 min <br>@Load 12.5 kg,<br> Temperature 232 °C	3.0 - 8.0 g/10 min <br>@Load 27.6 lb,<br> Temperature 450 °F	ASTM D1238
Arkema Group KYNAR FLEX® 2800-01 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical s..
Melt Flow	3.0 - 8.0 g/10 min <br>@Load 21.6 kg,<br> Temperature 232 °C	3.0 - 8.0 g/10 min <br>@Load 47.6 lb,<br> Temperature 450 °F	ASTM D1238
Arkema Group KYNAR® LBG2 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder.Applications: Membrane, Lithium ion battery applicationsInformation provided by Arkema Inc.
Melt Flow	3.0 - 8.0 g/10 min <br>@Load 12.5 kg,<br> Temperature 232 °C	3.0 - 8.0 g/10 min <br>@Load 27.6 lb,<br> Temperature 450 °F	ASTM D1238
Arkema Group KYNAR FLEX® 2850-00 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani..
Melt Flow	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
Polymer Resources PPX-FR3 Modified PPO, UL 94 V-1 with HDT of 265 F  (Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.