- Polymer Property : Environmental Stress Crack Resistance = 1000 hour
Polymer Property : Environmental Stress Crack Resistance = 1000 hour Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition A OR B, ASTM D1693, 100% Igepal |
|
NOVA Chemicals Novapol® HB-W747-A HDPE Extrusion Resin
Molded Plaque Properties. Features: High molecular weight, excellent ESCR, impact strength, easy processing.Data provided by the manufacturer.
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50; ASTM D1693 |
|
NOVA Chemicals Novapol® HE-Y449-A HDPE Extrusion Resin
Features: High ESCR, good toughness, good chemical resistance, good processability.Applications: Pipe coatings, profile extrusions, sheet extrusion for thermoforming, corrugated tubing, conduit.Data..
|
|||
| Environmental Stress Crack Resistance | 1000 hour | 1000 hour | |
|
NOVA Chemicals Sclair® 51-35BP HDPE Extrusion Resin
Features: Medium molecular weight, excellent ESCR, excellent toughness, good processability, good chemical resistance.Applications: Extrusion on to metal pipes to produce a corrosion resistant coati..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A (100% Igepal), F<sub>50</sub>; ASTM D1693 |
|
Formosa Plastics Formolene® L63550U Rotational Molding LLDPE
(discontinued **)
Hexene CopolymerApplications: Toys, medium tanks, material handling equipment and flat surface rotational molding applications.Formolene L63550 is fully heat and UV stabilized.Meets all requirements..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | (100% Igepal), F<sub>50</sub>; ASTM D1693 |
|
Formosa Plastics Formolene® L63935U Rotational Molding LLDPE
(discontinued **)
Hexene CopolymerApplications: Tanks, toys and other non-tank rotational molding applicationsFormolene L63935U is fully heat and UV stabilized.Meets all requirements of the U.S. Food and Drug Adminis..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 |
|
NIZHNEKAMSKNEFTEKHIM PE 6844G (446H7) High Density Polyethylene
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Temperature 50.0 °C
|
>=
1000
hour <br>@Temperature 122 °F
|
Conditions A, B and C; ASTM D 1693 |
|
Chevron Phillips Marlex® HHM TR-480Z/M362 Natural high density ethylene hexene copolymer/black concrete
(disc
Benefits: good long term hoop strength performance, very high melt strength, outstanding toughness even at low temperatures, concrete base resinCharacteristics: Pipe Ring ESCR > 2000 h, ASTM F 1248;..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Temperature 50.0 °C
|
>=
1000
hour <br>@Temperature 122 °F
|
Condition A; ASTM D 1693 |
|
Chevron Phillips Marlex® CL-200YB (Black) Rotational molding crosslinkable high density polyethylene
(discont
Benefits: crosslinks during molding - has outstanding melt strength at 204°C, is formulated to provide maximum UV protection for long-term outdoor weathering, contains an internal mold release, exc..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Temperature 50.0 °C
|
>=
1000
hour <br>@Temperature 122 °F
|
Condition A; ASTM D 1693 |
|
Chevron Phillips Marlex® CL-200YJN (Natural) Rotational molding crosslinkable high density polyethylene
(disc
Benefits: crosslinks during molding - has outstanding melt strength at 204°C, is formulated to provide maximum UV protection for long-term outdoor weathering, contains an internal mold release, exc..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Temperature 50.0 °C
|
>=
1000
hour <br>@Temperature 122 °F
|
Condition A; ASTM D 1693 |
|
Chevron Phillips Marlex® CL-200YNR JN (Natural) Rotational molding crosslinkable high density polyethylene
(d
Benefits: crosslinks during molding - has outstanding melt strength at 204°C, is formulated to provide maximum UV protection for long-term outdoor weathering, contains an internal mold release, exc..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 |
|
Chevron Phillips HiD® 9330 HDPE Natural Pipe Resin
(discontinued **)
Resin Type: gas phase linear hexane copolymer; ASTM D3350 Classification 335520A; ASTM D4976 Classification: PE 235, A 55701Applications: base resin for use in utility and conduit pipe applicationsI..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F0, ASTM D1693 |
|
NOVA Chemicals Sclair® 96A HDPE Extrusion Resin
(discontinued **)
Features: Excellent processability, excellent stretchability, superior strength, gel free.Applications: Oriented tapes for industrial woven bags and tarpaulins, monoaxial oriented films.Data provide..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F0, ASTM D1693 |
|
NOVA Chemicals Sclair® 96A-UV8D HDPE Extrusion Resin
(discontinued **)
Features: Excellent processability, excellent stretchability, superior strength, gel free, excellent UV resistance.Applications: Oriented tapes for industrial woven bags and tarpaulins, monoaxial or..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition C; ASTM D1693 |
|
ExxonMobil Escorene® LD-613 EVA Injection Molding Resin
(discontinued **)
Data provided by the manufacturer, Exxon Chemical.An 8.8% vinyl acetate copolymer resin designed for molding and extrusion applications requiring low temperatures, flexibility and toughness. This r..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition A; ASTM D1693 |
|
ExxonMobil Escorene® LD-409 EVA for Low Voltage Insulation
(discontinued **)
Data provided by the manufacturer, Exxon Chemical.A crosslinkable, 9.9% vinyl acetate copolymer designed for electrical applications.Applications: Designed to be blended with a suitable masterbatch ..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A - 10% Igepal®; ASTM D1693 |
|
LyondellBasell Petrothene® PR92735 Linear Low Density Polyethylene
ApplicationsPETROTHENE PR 92735 is a high molecular weight, linear low density-based compound designed for cable jacketing. PR 92735 contains a nominal carbon black content of 2.6% and antioxidant ..
|
|||
| Environmental Stress Crack Resistance | 1000 hour | 1000 hour | ASTM D1693 |
|
Global B-8200 High Density Polyethylene
Description-high molecular weight, excellent stress cracking resistance,
excellent impact strength to blow moldApplications-large drums, gasoline tanks, agricultural chemical tanksInformation provi..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | M F50; ASTM D1693 |
|
Micropol Microlink XL28/FR Black Crosslinkable Polyethylene
Flame retardant. Provides a finished molding of improved properties with the use of conventional rotational molding equipment. Properties include enhanced toughness (particularly low temp impact),..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition B, F50; ASTM D1693 |
|
IRPC Polimaxx Polene AM3245 PC High Density Polyethylene
CHARACTERISTICS:GOOD EXTRUDABILITYHIGH PRESSURE PIPE FOLLOW-UP MINIMUM REQUIRED STRENGTH OF 10.0 MPa (DESIGN STRESS OF 8.0 MPa) CLASSIFICATION PE100BLACK COLOR COMPOUNDAPPLICATIONS: PIPE EXTRUSIONSU..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition B, F50; ASTM D1693 |
|
IRPC Polimaxx Polene BM3245 PC High Density Polyethylene
CHARACTERISTICS:GOOD EXTRUDABILITYHIGH PRESSURE PIPE FOLLOW-UP MINIMUM REQUIRED STRENGTH OF 10.0 MPa (DESIGN STRESS OF 8.0 MPa) CLASSIFICATION PE100BLACK COLOR COMPOUNDAPPLICATIONS:PIPE EXTRUSIONSUI..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition B, 100% Igepal, F50; ASTM D1693 |
|
Ineos K44-06-122 HDPE
HDPE K44-06-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as ..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Thickness 3.00 mm,<br> Temperature 50.0 °C
|
>=
1000
hour <br>@Thickness 0.118 in,<br> Temperature 122 °F
|
Condition A, Compression Molded, 10% Igepal; ASTM D1693 |
|
Solvay Specialty Polymers Cogegum® AFR/765-UV Polyolefin
Cogegum® HFFR -Halogen Free Fire Retardant compound. Polyolefin based thermoplastic compound containing a fire retardant system that contributes to give the cable self-extinguish properties witho..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Thickness 3.00 mm,<br> Temperature 50.0 °C
|
>=
1000
hour <br>@Thickness 0.118 in,<br> Temperature 122 °F
|
Condition A, Compression Molded, 10% Igepal; ASTM D1693 |
|
Solvay Specialty Polymers Cogegum® AFR/920-UV Polyolefin
Flame Retardant; Good UV Resistance; Halogen Free; Low Smoke Emission; Low Toxicity; Self ExtinguishingUses: Cable Jacketing; Low Voltage Insulation; Wire & Cable ApplicationsExtrusion equipment: st..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Thickness 3.00 mm,<br> Temperature 50.0 °C
|
>=
1000
hour <br>@Thickness 0.118 in,<br> Temperature 122 °F
|
Condition A, Compression Molded, 10% Igepal; ASTM D1693 |
|
Solvay Specialty Polymers Cogegum® GFR/320 Polyolefin
Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Thickness 3.00 mm,<br> Temperature 50.0 °C
|
>=
1000
hour <br>@Thickness 0.118 in,<br> Temperature 122 °F
|
Condition A, Compression Molded, 10% Igepal; ASTM D1693 |
|
Solvay Specialty Polymers Cogegum® GFR/340-HP Polyolefin
Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly..
|
|||
| Environmental Stress Crack Resistance |
>=
1000
hour <br>@Thickness 3.00 mm,<br> Temperature 50.0 °C
|
>=
1000
hour <br>@Thickness 0.118 in,<br> Temperature 122 °F
|
Condition A, Compression Molded, 10% Igepal; ASTM D1693 |
|
Solvay Specialty Polymers Cogegum® GFR/350 Polyolefin
Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a pol..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F0, ASTM D1693 |
|
NOVA Chemicals Sclair® 94D1 HDPE Extrusion Resin
(discontinued **)
Features: Excellent processability, high stretchability, excellent strength.Applications: Package nettings for produce, Christmas tree wrap and turkey overwrap.Data provided by the manufacturer.
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | 100% ant.; ASTM D1693-70 |
|
Total Finacene® BM359SG HDPE, blow molding
(Unverified Data**)
FINACENE® BM359 SG has been especially designed for the manufacture of blow moulded bottles (up to 5 liters) with a superior surface gloss and contact transparency. It is recommended either in mono..
|
|||
| Environmental Stress Crack Resistance | 1000 - 5000 hour | 1000 - 5000 hour | Average value: 2290 hour Grade Count:10 |
|
Overview of materials for Medium Density Polyethylene (MDPE), Extruded
This property data is a summary of similar materials in the MatWeb database for the category "Medium Density Polyethylene (MDPE), Extruded". Each property range of values reported is minimum and max..
|
|||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition B, ASTM D1693, 100% Igepal |
|
NOVA Chemicals Novapol® TR-0535-UG Hexene MDPE Rotational Molding Resin
(discontinued **)
Molded Plaque Properties. Features: excellent impact strength, excellent ESCR.Applications: large parts, agricultural storage tanks.Data provided by the manufacturer.
|
|||