- Polymer Property : Linear Mold Shrinkage, Flow = 0.0050 cm/cm
Polymer Property : Linear Mold Shrinkage, Flow = 0.0050 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC
LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific)
LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI (Asia Pacific)
LNP* Lubricomp* EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific)
LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Flow |
0.0040
-
0.0050
cm/cm @Thickness 3.20 - 4.60 mm |
0.0040
-
0.0050
in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific)
40% GR, increased strength/stiffness vs unreinforced. Non-flame retardant. For appliance handles, spotlights, electric motors, pump housings etc.This data was supplied by SABIC-IP for the Asia Pacif..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 420M PBT (Asia Pacific)
30% GR PBTP. Easy flow/release. High stiffness and load bearing properties.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 508 PBT+PC
30% GR PBT+PC. Excellent mechanical and thermal performance. Non-flame retardant. Reduced warpage characteristics. Applications same as VALOX 420.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON DX05474 PC
LNP* STAT-KON* DX05474 is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant, Mold ..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-KON DX05474 PC (Asia Pacific)
LNP* Stat-kon* DX05474 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Ret..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 830 PBT
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® 830 PBT (Asia Pacific)
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HR426 PBT (Asia Pacific)
AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6
LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americ..
|
|||
| Linear Mold Shrinkage, Flow |
0.0020
-
0.0050
cm/cm @Time 86400 sec |
0.0020
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP AX02749 ABS
LNP* THERMOCOMP* AX02749 is a compound based on ABS containing proprietary fillers.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI
LNP* Thermocomp* EF004 is a compound based on Polyetherimide resin containing 20% Glass Fiber.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS
LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS (Asia Pacific)
LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66
LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66
LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HX420HP PBT
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Thickness 1.50 - 3.20 mm |
0.0030
-
0.0050
in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® HX420HP PBT (Europe-Africa-Middle East)
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT
LNP* STAT-LOY* WF306C is a compound based on PBT resin containing 30% Glass Fiber. Added features of this material include: Antistat, Clean Compound System.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT (Asia Pacific)
LNP* Stat-loy* WF306C is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: Antistat, Clean Compounding System.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Thermocomp 5C003
LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as THERMOCOMP* FP-VC..
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP AH0400A ABS
LNP* THERMOCOMP* AH0400A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC
LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Flame Retardant.
|
|||
| Linear Mold Shrinkage, Flow |
0.0017
-
0.0050
cm/cm @Time 86400 sec |
0.0017
-
0.0050
in/in @Time 24.0 hour |
ISO 294 |
|
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6
LNP THERMOCOMP* PF006U is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of thie grade are: UV Stabilized.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific)
LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Flow |
0.0030
-
0.0050
cm/cm @Time 86400 sec |
0.0030
-
0.0050
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Asia Pacific)
LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Flow |
0.0020
-
0.0050
cm/cm @Time 86400 sec |
0.0020
-
0.0050
in/in @Time 24.0 hour |
ASTM D 955 |
|
SABIC Innovative Plastics LNP Verton WV007XXP PBT (Europe-Africa-Middle East)
LNP VERTON* WV007XXP is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
Copyright © lookpolymers.com All Rights Reserved