Polymer Property : Linear Mold Shrinkage, Flow = 0.0080 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP COLORCOMP D1000P PC
LNP* COLORCOMP* D1000P is an unfilled Polycarbonate. Added feature of this grade is: Exceptional Processing.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP COLORCOMP D1000P PC (Asia Pacific)
LNP* Colorcomp* D1000P is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Exceptional Processing.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES
LNP COLORCOMP* JX91550 is an unfilled Polyethersulfone.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific)
LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific)
LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS
LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East)
LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC
LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific)
LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 420 PBT (Asia Pacific)
30% GR, excellent strength, stiffness and dimensional stability. High heat resistance. Appliance handles, spotlights, electric motors, connectors.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 1.50 - 3.20 mm
 0.0060 - 0.0080 in/in

@Thickness 0.0591 - 0.126 in
 SABIC Method
SABIC Innovative Plastics Valox® 457 PBT
6.5% GR PBT, UL94 V-0/5V.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 553 PBT+PC
30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 553 PBT+PC (Asia Pacific)
30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP STAT-KON DX04462C PC
LNP STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP STAT-KON DX04462C PC
LNP STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 830 PBT
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 865 PBT+PET
30% GR PBTP, UL94 V-0 rated. Non-blooming flame retardant. Improved surface appearance. Same application areas as for VALOX 855.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® HR426 PBT (Asia Pacific)
AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 6.40 mm
 0.0060 - 0.0080 in/in

@Thickness 0.252 in
 SABIC Method
SABIC Innovative Plastics Valox® VIC4311 PBT
VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 6.40 mm
 0.0060 - 0.0080 in/in

@Thickness 0.252 in
 SABIC Method
SABIC Innovative Plastics Valox® VIC4311 PBT (Asia Pacific)
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific)
LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D 955
SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12
LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP STAT-KON DX04462C PC (Asia Pacific)
LNP* STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Clean Compounding System.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 420SE0U PBT (Asia Pacific)
UV-Stabilized version of 420SE0.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 430 PBT (Asia Pacific)
33 % glass reinforced, impact modified. Connectors, etc.
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 508 PBT+PC (Asia Pacific)
30% GR PBT+PC. Excellent mechanical and thermal performance. Non-flame retardant. Reduced warpage characteristics. Applications same as VALOX 420.
Linear Mold Shrinkage, Flow 0.0030 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
SABIC Innovative Plastics Valox® HX420HP PBT (Europe-Africa-Middle East)
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® HX420HP PBT (Europe-Africa-Middle East)
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D 955
SABIC Innovative Plastics LNP Thermocomp MF006S PP (Asia Pacific)
LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia P..
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP MF006SU PP
LNP* THERMOCOMP* MF006SU is a compound based on Polypropylene containing 30% lass Fiber. Characteristics of this grade are: Heat Stabilized, Chemically Coupled, UV Stabilized.