Polymer Property : Compressive Strength = 165 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Compressive Strength	165 MPa	23900 psi	ASTM D695
Premix Premi-Glas® 1200H-20 Polyester SMC Premi-Glas® 1200H-20 is a 20% fiberglass reinforced, thermoset, Sheet Molding Compound designed for applications where good arc resistance and dielectric strength are required and UL 94HB flame rec..
Compressive Strength	165 MPa <br>@Temperature 23.9 °C	24000 psi <br>@Temperature 75.0 °F	Dry; 325°F Autoclave; ASTM D695
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Aerospace Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz..
Compressive Strength	165 MPa <br>@Temperature 23.9 °C	24000 psi <br>@Temperature 75.0 °F	Dry; ASTM D695
Park Electrochemical Nelcote® S-860 Silicone Prepreg, 1581-112NPH E-Glass Reinforced Nelcote® S-860 is a MIL-P-25518 type silicone resin with a good combination of electrical and high temperature properties. GMS4001 qualified specificationsKey Features and Benefits:500°F maximum s..
Compressive Strength	165 MPa	24000 psi	10% Def.; ASTM D695
Quadrant EPP Duratron® PAI T4203 Extruded Polyamide-imide (ASTM Product Data Sheet)
Compressive Strength	165 MPa	24000 psi	10% Def.; ASTM D695
Quadrant EPP Semitron® MPR-1000 (ASTM Product Data Sheet)
Compressive Strength	165 MPa	24000 psi	10% Def.; ASTM D695
Quadrant EPP Techtron® PSGF PPS - Compression Molded 40% Glass Reinforced Polyphenylene Sulfide (ASTM Product Data Sheet)
Compressive Strength	165 MPa	23900 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ X65 Phenolic Formaldehyde Resin, UL Listed  (discontinued **) Phenolic molding compound, inorganically/organically filled, good heat-resistance and dimensional stability, UL listed molding compound 3.0 mm/V-0 (BN, BK).Application areas: Oven strips.Information..
Compressive Strength	165 MPa	23900 psi	ASTM D695
IDI Composites 48-50 Thermoset Polyester, Molding Moderate strength electrical grade with good track resistance and V-O flame resistance.Data provided by the manufacturer.
Compressive Strength	165 MPa	23900 psi	ASTM D695
IDI Composites A-203 Thermoset Polyester, Sheet AUTOMOTIVE - Versatile family of compounds specifically designed for automotive structural applications. Low shrink characteristics, heat resistance, long-term dimensional stability, and corrosion r..
Compressive Strength	165 MPa	23900 psi	ASTM D695
IDI Composites E-203 Thermoset Polyester, Sheet ELECTRICAL - U.L. recognized (E53587). Versatile family of compounds designed to meet the most demanding electrical and electronic applications. Excellent dielectric properties and arc/track resista..
Compressive Strength	>= 165 MPa	>= 24000 psi
Master Bond EP46HT-2Med Two Component Heat Resistant Biocompatible Epoxy System Master Bond Polymer System EP46HT-2MED is a two component medical grade epoxy system for high performance structural bonding and casting suitable for applications where resistance to temperatures fr..
Compressive Strength	165 MPa	23900 psi	ASTM D695
Plenco 2369 Phenolic, Granular, Compression Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369..
Compressive Strength	165 MPa	23900 psi	ASTM D695
Plenco 4309 Phenolic, Nodular, Injection Molded PLENCO 04309 is a heat resistant, glass reinforced phenolic molding compound offering improved mechanical strength and electrical strength properties. UL recognized under component file E40654. 0430..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/8" to 1" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/16" to 1/4" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/8" to 1" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	ASTM D695
Applied Composites 8038 Polyester SMC Industry Application: TransportationProduct Application: Mass TransitDistinct Features: Low Smoke Construction and Mass Transit, Oxygen Matex 80+, E84-61 TunnelInformation provided by Applied Compos..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 605LS Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605LS molding compound is a low-shrink, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good mol..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 610 Mineral filled, glass-fiber-reinforced polyester compound BMC 610 molding compound is a mineral filled, glass fiber reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is set a part form other medium impact..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Polyester Flat Sheet 1/8" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/8" to 1" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 5338 Mineral Filled, Glass Reinforced Polyester BMC 5338 molding compound is a mineral Filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced in ex..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 610 Mineral Filled, Glass Reinforced Polyester Compound BMC 610 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is set a part form other medium impact el..
Compressive Strength	165 MPa	23900 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 8052 Phenolic Formaldehyde Resin, Resistant to High Temperatures  (discontinued **) Phenolic molding compound, glass fiber reinforced and inorganically filled. Excellent heat resistance with respect to surface finish and mechanical properties.Application areas: Pan handles, heat r..