Polymer Property : Modulus of Elasticity = 214 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816Â°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa	31000 ksi	sheet at RT
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370Â°C (700Â°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595Â°C (1100Â°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, room temperature after 25% cold reduction, 1175Â°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, room temperature sheet after 2500 hours of 650Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, room temperature sheet after 500 hours of 650Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, room temperature sheet after 500 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa @Temperature 200 Â°C	31000 ksi @Temperature 392 Â°F
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity	214 GPa	31000 ksi
Latrobe DuraTechâ„¢ 20CV Powder Metal Stainless Tool Steel DuraTech 20CV is a highly wear resistant, powder metallurgy stainless tool steel. The steel contains a large volume of extremely hard vanadium carbides, which provide excellent wear resistance. Du..
Modulus of Elasticity	214 GPa	31000 ksi
Latrobe DuraTechâ„¢ M48 Powder Metal High Speed Steel (ASTM M48) DuraTech M48 super high speed steel is a high-performance high speed steel which exhibits superior hot (red) hardness compared to T15 and M42 high speed steels, and wear resistance comparable to tha..
Modulus of Elasticity	214 GPa	31000 ksi
Crucible Steel CPM® Rex M4 HC(HS) Tool Steel CPM REX M4 HC(HS) is a high vanadium special purpose high speed steel exhibiting better wear resistance and toughness than M2 or M3 in cold work punches, die inserts and cutting applications involvi..
Modulus of Elasticity	214 GPa @Temperature 399 °C	31000 ksi @Temperature 750 °F	hardened and tempered
Bohler-Uddeholm UDDEHOLM VANADIS 30 AISI M2 + Co SUPERCLEAN 3 Powder Metallurgical Cold Work Tool Steel Uddeholm Vanadis 30 is a Co high alloyed powder metallurgy high speed steel corresponding to AISI M3:2 + Co. The high compressive strength, 67 HRC, and good abrasive wear resistance makes Uddeholm V..
Modulus of Elasticity	214 GPa	31000 ksi
Carpenter Micro-Melt® HS-76 Alloy (AISI M48) Micro-Melt® HS-76 alloy is a super high speed steel possessing abrasion resistance equal to T15 and superior red hardness to T15 and M42. It is heat treatable to HRC 70 and is a good candidate for ..
Modulus of Elasticity	214 GPa	31000 ksi
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information..
Modulus of Elasticity	214 GPa @Temperature 200 °C	31000 ksi @Temperature 392 °F
Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity	214 GPa @Temperature 200 °C	31000 ksi @Temperature 392 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity	214 GPa @Temperature 200 °C	31000 ksi @Temperature 392 °F
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity	214 GPa @Temperature 200 °C	31000 ksi @Temperature 392 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity	214 GPa @Temperature 200 °C	31000 ksi @Temperature 392 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity	214 GPa @Temperature 200 °C	31000 ksi @Temperature 392 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity	214 GPa	31000 ksi
Latrobe DuraTech™ 30 Powder Metal High Speed Steel (ASTM M3-2) DuraTech 30 super high speed steel is based upon the chemical composition of ASTM M3-2 high speed steel, but with the addition of over 8% cobalt. DuraTech 30 can be heat treated to 68 HRC. The high ..