Polymer Property : Flexural Strength = 100 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	100 MPa	14500 psi	ASTM D790
Premix Premi-Glas® 2205-15 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2205-15 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal ..
Flexural Strength	<= 100 MPa	<= 14500 psi	ISO 178
Polykemi AB POLYblend 85FS PC/ABS-Blend Information provided by Polykemi AB
Flexural Strength	<= 100 MPa	<= 14500 psi	ISO 178
Polykemi AB SCANMID 6 B32^ E Q30 Nylon 6, Glass Fiber Reinforced, Modified Information provided by Polykemi AB
Flexural Strength	100 - 130 MPa	14500 - 18900 psi	Injection; ISO 178
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically..
Flexural Strength	100 - 130 MPa	14500 - 18900 psi	Compression; ISO 178
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Flexural Strength	100 MPa	14500 psi
Poco Graphite EDM-AF5 EDM Graphite POCO's EDM-AF5 is the only graphite electrode material available on the market today with an average particle size of less than one micron. This particle structure gives EDM-AF5 superior strength, p..
Flexural Strength	100 MPa	14500 psi	ASTM D790
PolyOne Edgetek® AS-30GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled  (discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Flexural Strength	100 - 120 MPa	14500 - 17400 psi	Injection; ISO 178
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Flexural Strength	100 MPa <br>@Temperature 22.8 °C	14500 psi <br>@Temperature 73.0 °F	ASTM D790
Ensinger Sintimid™ V 40% graphite Polyimide (PI)  (discontinued **) SINTIMID™ V polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an idea choice for the most demanding applications. SINTIMID™ V..
Flexural Strength	100 MPa	14500 psi
Lehmann & Voss LUVOCOMÂ® 50-7164/BL02 Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Reduced moment of inertia compared with metal parts.Low warpag..
Flexural Strength	100 MPa	14500 psi	ISO 178
Lucite International DiakonÂ® ST25H8 Toughened Acrylic Compound The DiakonÂ® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness.The grades in the DiakonÂ® series can be processed by..
Flexural Strength	100 MPa	14500 psi	ASTM D790
FiberfilÂ® J-62/30/E8 Polypropylene Copolymer, 30% Glass Fiber Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics
Flexural Strength	100 MPa	14500 psi	2 mm/min; ISO 178
Ineos ABS LustranÂ® ABS 150G10 10% Glass Fiber Reinforced Grade
Flexural Strength	100 MPa	14500 psi	ISO 178
Grupo Repol DinalonÂ® B1X25 V0 PA6 V0 Red Phosphorus and Halogen Free Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Strength	100 MPa	14500 psi	2 mm/min; ISO 178
Hexion UP 802 Unsaturated Polyester Resin, High Surface Quality, Low Shrinkage, High Arc Resistance Polyester molding compound, inorganically filled, glass fiber reinforced, styrene free, high dimensional stability, very slight post shrinkage, good mechanical properties, increased electrical value..
Flexural Strength	100 MPa	14500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL V01525 PPE+HIPS Noryl* V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t..
Flexural Strength	100 MPa	14500 psi	ISO 178
SABIC Innovative Plastics LNP Thermocomp AF0029 ABS LNP* Thermocomp* AF0029 is an ABS base resin containing Glass Fiber. Characteristics of this grade are Flame Retardancy.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	100 MPa	14500 psi	ISO 178
Styrolution LuranÂ® S KR 2864 C Colored ASA+PC Description: Easy flowing injection molding grade with heat resistance for parts with thin walls and/or with adverse flowpath/wall thickness ratios.Applications: Mobile phone housings.Information pr..
Flexural Strength	100 MPa	14500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 4512 PBT+PC (Europe-Africa-Middle East) 10% GF FR PBT/PC Blend
Flexural Strength	100 MPa	14500 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WH0245A PBT (Asia Pacific) LNP THERMOCOMP* WH0245A is a compound based on Polybutylene Terephalate resin. Added features of this material include: High Specific Gravity.
Flexural Strength	100 MPa	14500 psi
Master Bond EP46HT Epoxy Adhesive for Structural Bonding Description: Master Bond System EP46HT is a newly formulated two component high performance heat resistant epoxy resin system with excellent mechanical strength and chemically resistant properties f..
Flexural Strength	100 MPa	14500 psi	ASTM D790
Polyram PlusTek PB150 Nylon 6, Injection Molding Fast cycle polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	100 MPa	14500 psi	ASTM D790
A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene DescriptionPolyfort® FPP 1606 is a 30% glass filled chemically coupled impact copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	100 MPa	14500 psi	ASTM D790
CPC - Vycom FLAMETEC™ CPVC Chlorinated Polyvinyl Chloride Sheet Flametec™ CPVC made from Corzan® 4910 white 120 compound is a high heat, corrosion resistant chlorinated polyvinyl chloride sheet. Because of its excellent corrosion resistance at elevated tempera..
Flexural Strength	>= 100 MPa	>= 14500 psi	Perpendicular to laminations; IEC 1212-2 5.1
Hippe PF WV 201 Wood veneer Reinforced Phenolic Resin - Sheet Cross plied. Used in mechanical applications. Good mechanical properties.Information provided by Hippe.
Flexural Strength	>= 100 MPa <br>@Diameter >=100 mm	>= 14500 psi <br>@Diameter >=3.94 in	Perpendicular to laminations; IEC 1212-2 4.1
Hippe PF CP 22 Cellulose Paper Reinforced Phenolic Resin - Round, Rolled Tube High-voltage, electrical applications at power frequencies. High electric strength in oil.Information provided by Hippe.
Flexural Strength	<= 100 MPa	<= 14500 psi	dry; ISO 178
Azoty Tarnow™ Tarnamid® T-27 CFHI Polyamide 6 - Antistatic and Electroconductive Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffn..
Flexural Strength	100 MPa	14500 psi	ISO 178
BASF Ultradur® B 4300 K4 20% Glass Bead Filled PBT Description: Is a PBT + ASA, Injection-molding grades containing 20% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit..