Polymer Property : Flexural Strength = 103 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	103 MPa	15000 psi	ASTM D790
Niche Polymer PA6BK Nylon 6 Information provided by Niche Polymer
Flexural Strength	103 MPa	15000 psi	ASTM D790
Polymer Resources TPSF-G10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced Polybutylene Terephthalate, Structural Foam, 10% Glass ReinforcedProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Info..
Flexural Strength	103 MPa	14900 psi	1.3 mm/min; ASTM D790
PolyOne Edgetek® X TR2-10GF/000 NATURAL Copolyester The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Ea..
Flexural Strength	103 MPa	14900 psi	ASTM D790
SABIC Innovative Plastics LNP COLORCOMP NX05467 PC+ABS LNP* COLORCOMP* NX05467 is an unfilled Polycarbont+ABS resin. Added features of this grade are: Non-Chlorinated, Non-Brominated Flame Retardant.
Flexural Strength	103 MPa	14900 psi
Haysite 30000 Polyester BMC, 15% Glass Reinforced Haysite 30000 series bulk molding compound is a general purpose material. This compound can be compression, transfer, or injection molded. This material has good mechanical properties and can be pig..
Flexural Strength	103 MPa	14900 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RAP22 PA 66 LNP* LUBRICOMP* RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant.
Flexural Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP AF006 ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
Flexural Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP IB008 PA 6/12 (Europe-Africa-Middle East) LNP* Thermocomp* IB008 is a compound based on Nylon 6/12 resin containing Glass Bead.
Flexural Strength	103 MPa	14900 psi	ISO 178
Styrolution Polystyrol 158 K GR 21 PS Description: Polystyrol 158 K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blend s with high impact Polystyrol in heat contact applicati..
Flexural Strength	103 MPa	14900 psi	2.8 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VG-4920F ABS, Glass Filled FR Information provided by Samsung Cheil Industries.
Flexural Strength	103 MPa	14900 psi	at rupture; ASTM D790
Sumitomo Bakelite North America EM 7302XLD Long Glass Fiber Reinforced Epoxy EM 7302XLD is a long fiberglass reinforced epoxy molding compound with a low density inert filler. This compound is designed for applications where moderate strength and weight savings are desirable..
Flexural Strength	103 MPa	14900 psi
Cosmic Plastics 6130F Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer.
Flexural Strength	103 MPa	14900 psi	Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-750V5T A9T Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High dimensional stability; High fatigue strength; High weather resistance; Good fire behavior; Suitable for vacuum; Good machinability; Contains PTFE; Stre..
Flexural Strength	103 MPa	15000 psi	ASTM D790
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	103 MPa	14900 psi	2 mm/min; ISO 178
Eurostar Starflam PK0049 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded Starflam PK0049 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	103 MPa	15000 psi	ASTM D790
Asahi Kasei Thermylene® P6-23FG-2600 23% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil
Flexural Strength	103 - 138 MPa	15000 - 20000 psi
Bulk Molding Compounds BMC 880 Medium Strength Molding Compound BMC 880 is a medium strength, low shrink molding compound designed for outdoor applications. This material is UL Listed 94-V0/5V and is UL approved for outdoor use. It can be supplied in bulk or ext..
Flexural Strength	103 - 138 MPa	15000 - 20000 psi
Bulk Molding Compounds BMC 1901 Mineral Filled Alkyd BMC 1901 molding compound is a mineral filled, glass-fiber-reinforced alkyd compound suitable for compression transfer molding. It is a general purpose with medium impact strength and good overall e..
Flexural Strength	103 MPa	14900 psi	ASTM D790
Ashley Polymers Ashlene® R6043 Nylon 6 Medium viscosity extrusion grade Nylon 6 resin with excellent melt stability, good melt strength: suitable for extrusion coating and film co-extrusion applications. Excellent grease resistance, tou..
Flexural Strength	103 MPa	15000 psi	2.0 in/min; ASTM D790
LTL Color Compounds ColorFast® FRPC310 Polycarbonate, Flame-Retarded V0-rated 10% glass-filled polycarbonate, excellent impact strengthAll information provided by LTL Color Compounders, Inc.