Polymer Property : Flexural Strength = 10300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
PolyOne Geon™ Vinyl Rigid Molding M5240 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of..
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
PolyOne Geon™ Vinyl Rigid Molding M5700 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of..
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
Eastman Eastar GN125 Copolyester, Natural  (discontinued **) Eastar Copolyester GN125 is a glycol modified polyethylene terephthalate (PET) that contains an ultraviolet light inhibitor. This product is recommended for indoor applications requiring enhanced co..
Flexural Strength	71.0 MPa	10300 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific) LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
SABIC Innovative Plastics NORYL SE100P PPE+HIPS (Asia Pacific)
Flexural Strength	71.0 MPa	10300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon CX01039 PS (Europe-Africa-Middle East) LNP* Stat-kon* CX01039 is a compound based on Polystyrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP..
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
Techmer ES HiFill FRÂ® ABS FR Availability: North AmericaForms: PelletsFeatures: Flame RetardantTPCI# 1039121Information provided by TP Composites, Inc.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
Techmer ES HiFill FRÂ® ABS FR UV BK Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Flame Retardant and Good UV ResistanceUL File Number: E157318Appearance: BlackTPCI# 9224121Information provided by TP Compos..
Flexural Strength	71.0 MPa	10300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance.
Flexural Strength	71.0 MPa	10300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance.
Flexural Strength	71.0 MPa	10300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. High flow with good impact and excellent optical quality.This data was supplied by SABIC-IP for the Europe-Africa-Middle East..
Flexural Strength	71.0 MPa	10300 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP 9X04488 POLYPHENYLENESULFONE (Asia Pacific) LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.
Flexural Strength	71.0 MPa	10300 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP 9X04488 PPS LNP* THERMOCOMP* 9X04488 is a compound based on PPS resin containing Mineral.
Flexural Strength	71.0 MPa	10300 psi	ASTM Test
Styrolution LuranÂ® S 778 T ASA Luran S 778 T is an injection molding ASA grade with enhanced toughness and heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Flexural Strength	71.0 MPa	10300 psi	ASTM D 790
SABIC Innovative Plastics Noryl EBN90 PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi
Cosmic Plastics ID-40 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman.
Flexural Strength	71.0 MPa	10300 psi	15mm/min; ASTM D790
Denka MALECCA K-510 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
Ensinger Tecatron® XP-71 Compression Molded PPS Compound, 20% PTFE Filled Natural Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p..
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	71.0 MPa	10300 psi	ASTM D790
Techmer ES Plastiblend® ABS 922 NAT Availability: North AmericaForms: PelletsInformation provided by TP Composites, Inc.
Flexural Strength	71.0 MPa	10300 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp GL004 PSU LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas re..
Flexural Strength	71.0 MPa	10300 psi	2 mm/min; ISO 178
Sax Polymers SAXALEN PPH121GK30 Polypropylene Homopolymer, 30% Glass Filled SAXALEN PPH121GK30 is a 20% glass-fiber and 10% glass-beads filled Polypropylene - Homopolymer intended for injection molding. This type has a higher stiffness and a optimized warpage grade.Informat..