Mechanical Properties	Metric	English	Comments
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	Injection; ISO 178
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	Injection; ISO 178
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin..
Flexural Strength	120 - 160 MPa	17400 - 23200 psi	Injection; ISO 178
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Flexural Strength	120 - 160 MPa	17400 - 23200 psi	Injection; ISO 178
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	Injection; ISO 178
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe..
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	Injection and Compression; ISO 178
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very ..
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	Injection; ISO 178
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Flexural Strength	140 - 160 MPa	20300 - 23200 psi	At Rupture; ISO 178
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group