Polymer Property : Flexural Strength = 186 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	186 MPa	27000 psi	ASTM D790
PolyOne Trilliant™ HC HC3220-0030 RS Natural Polycarbonate (PC) The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead..
Flexural Strength	186 MPa	27000 psi	ASTM D790
Polymer Resources TP-G20 Polybutylene Terephthalate, 20% Glass Reinforced Polybutylene Terephthalate, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information prov..
Flexural Strength	186 MPa	27000 psi	ASTM D790
Polymer Resources TPSF-G30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf..
Flexural Strength	186 MPa	27000 psi	ASTM D790
PolyOne Edgetek® NL-20GF/000 Nylon 6/12, Glass Filled  (discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Flexural Strength	186 MPa	27000 psi	ASTM D 790
SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Flexural Strength	186 MPa	27000 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DEF42 PC LNP STAT-KON* DEF42 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	186 MPa	27000 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON REL42 PA 66 LNP* STAT-KON* REL42 is a compound based on Nylon 66 resin containing 20% PTFE, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Flexural Strength	186 MPa	27000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IF004 PA 6/12 (Asia Pacific) LNP* Thermocomp* IF004 is a compound based on Nylon 6/12 resin containing Glass Fiber.
Flexural Strength	186 MPa	27000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP JF006E PES LNP* THERMOCOMP* JF006E is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
Flexural Strength	186 MPa	27000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC LNP* Thermocomp* Lexan_LGN5030 compound is a glass reinforced. Flame retardant.
Flexural Strength	186 MPa	27000 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries.
Flexural Strength	186 MPa	27000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP PF005S PA 6 LNP* THERMOCOMP* PF005S is a compound based on Nylon 6 resin containing 25% Glass Fiber. Added features of this material include: Heat Stabilized.
Flexural Strength	186 MPa	27000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RFB53XXZ PA 66 LNP* THERMOCOMP* RFB53XXZ is a compound based on Nylon 66 resin containing 15% Glass Fiber, 25% Glass Bead.
Flexural Strength	186 MPa	27000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT LNP* THERMOCOMP* WF006H is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
Flexural Strength	186 MPa	27000 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX RNX130 PPE+PS+PA 30% glass reinforced PPE+PS+PA alloy for automotive and nonautomotive applications. Recycle grade in black/gray only.
Flexural Strength	186 MPa	27000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp LF004 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF004 Is a compound based on Polyetheretherketone containg Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Strength	186 MPa	27000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOTUF VX00585 PA 66 (Asia Pacific) LNP* Thermotuf* VX00585 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.
Flexural Strength	186 MPa	27000 psi	ASTM D790
A. Schulman ComAlloy® E-17036 Glass Fiber Reinforced High Heat Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	186 MPa	27000 psi	ASTM D790
A. Schulman ComAlloy® E-17036 Glass Fiber Reinforced High Heat Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	186 MPa	27000 psi	ASTM D790
PolyOne Lubri-Tech™ NI-10CF/15T Nylon 6/10, Carbon Fiber Reinforced, PTFE Lubricated  (discontinued **) Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Flexural Strength	186 MPa	27000 psi	ASTM D790
LNP Thermocomp® JF-1006 BK8-115 Polyethersulfone, Glass Fiber Reinforcement  (discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..