Polymer Property : Flexural Strength = 260 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	260 MPa	37700 psi	ASTM D790
NYCOA 5033 HS 33% Glass-Fiber Reinforced, Heat Stabilized, Nylon 66 Resin NYCOA 5033 HS is a 33% glass fiber reinforced, heat stabilized Nylon 66 resin used for injection molding. It offers an outstanding balance of mechanical properties over standard grades of convention..
Flexural Strength	260 MPa	37700 psi
Plastcom SLOVAMID 66 GF 25 FRI 2 PA66, 25% glass fibre, flame retardant FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fibre and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 in accordance with UL 94. Non..
Flexural Strength	260 MPa	37700 psi
Lehmann & Voss LUVOCOMÂ® 1105-8168 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts at high movement velocity.High chemical resista..
Flexural Strength	260 MPa	37700 psi
Lehmann & Voss LUVOCOMÂ® 1114-8364 PAEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Electrically conduct..
Flexural Strength	260 MPa	37700 psi	ISO 178-A
Lanxess DurethanÂ® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
Flexural Strength	260 MPa	37700 psi
Lehmann & Voss LUVOCOMÂ® 1-0935 Polyamide 66, with glass fiber and PTFE, 8-mm-granulate Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec..
Flexural Strength	260 MPa	37700 psi
Lehmann & Voss LUVOCOMÂ® 1105/GF/30/NAT-2 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Strength	260 MPa	37700 psi	5 mm/min; ISO 178
Gromax CFG35-R113N1 Nylon 6 36% Glass Filled (Dry) Information provided by Gromax Enterprises Corp.
Flexural Strength	260 MPa	37700 psi	ASTM D790
Solvay TECHNYLÂ® A 218 V25 NAT BA PA66, 25% glass fiber, DRY Description: Polyamide 66, reinforced with 25% of glass fiber, specially stabilized to improve its resistance to oils and greases, for injection molding.Available in: Asia PacificProduct Application..
Flexural Strength	260 MPa	37700 psi	ISO 178
Solvay TECHNYLÂ® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY Provisional datasheet - Product in developmentDescription: Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYLÂ..
Flexural Strength	260 MPa	37700 psi	ISO 178
Solvay TechnylÂ® C216V25 25% Glass Filled Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay.
Flexural Strength	260 MPa	37700 psi	ISO 178
Solvay TECHNYLÂ® A 20 V35 PA66, 35% glass fiber, DRY Description: Flame retardant polyamide 66, reinforced with 35% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America.Product Applications: This ph..
Flexural Strength	260 MPa	37700 psi	ASTM C1161
M Cubed Technologies HSC-702 Aluminum-toughened Reaction Bonded Silicon Carbide High fracture tougness reaction bonded SiC. Used in applications that require both high wear and high impact resistance. Bullnoses, fan liners, hydrocyclone liners, etc.Information provided by M C..
Flexural Strength	260 MPa	37700 psi	ISO 178
Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd.
Flexural Strength	260 MPa	37700 psi	ISO 178-93
Wellman Wellamid® GF43-66/6 XE-NBK1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66/6Information provided by Wellman.
Flexural Strength	260 MPa	37700 psi	dry; ISO 178
DSM Novamid® 1013G30 1 NA PA6-GF30 30% Glass Reinforced, Injection Molding
Flexural Strength	260 MPa	37700 psi	2 mm/min; ISO 178
Eurostar Staramide AG6H PA66, 30% Glass Filled, Injection Molded AG6 is a Heat Stabilized, 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Flexural Strength	260 MPa	37700 psi	2 mm/min; ISO 178
Eurostar Staramide RF006SXS PA66, 30% Glass Fiber Filled, Injection Molded Staramide RF006SXS is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006HS)Information provided by Eurostar.
Flexural Strength	260 MPa	37700 psi	2 mm/min; ISO 178
Eurostar Starflam AFR470X2 PA66, 35% Glass Filled, Injection Molded AFR470X2 is a Red Phosphorous, Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli..
Flexural Strength	260 MPa	37700 psi	Elastic Limit in Bending, direction of rolling
CLAL-MSX CUPROROR® TL5 Spring, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat..
Flexural Strength	260 MPa	37700 psi	dry; ISO 178
DSM EcoPaXX® Q-HG6 PA410-GF30 30% Glass Reinforced, Heat Stabilized
Flexural Strength	260 MPa	37700 psi	Longitudinal direction; ISO 178
Azdel Plus U421-B01 42% Directionalized Continuous Fiber Mat / PP Resin Matrix AZDEL® U421-B01 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat and oriented fiber mat contained within a polypropylene resin matrix. This co..
Flexural Strength	260 MPa	37700 psi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® A3 GF 25 (2420) PA 6.6 Dry, 25% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Flexural Strength	<= 260 MPa	<= 37700 psi	dry, 3.5% flexure; ISO 178
Azoty Tarnow™ Tarnamid® T-27 GF30 Polyamide 6 - Glass Fiber Reinforced 30% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..
Flexural Strength	260 MPa	37700 psi	ASTM Test
BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion ..
Flexural Strength	260 MPa	37700 psi	ISO 178
BASF Ultramid® B3WG6 GP BK 23210 30% Glass Filled PA6 (Dry) Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade used e.g. for automobile manifold.Information provided by BASF
Flexural Strength	260 MPa	37700 psi
Lehmann & Voss LUVOCOM® 1-7233-1 Polyamide 66, with glass fiber, PTFE, lubricant modified, silicone-free Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, ..