Polymer Property : Flexural Strength = 26100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 180 MPa	<= 26100 psi	ISO 178
Polykemi AB POLYshine PBT D311 GF30 PBT, Glass-Fiber Reinforced, Modified Information provided by Polykemi AB
Flexural Strength	180 MPa	26100 psi	STN EN ISO 178
Plastcom SLOVAMID 6 GF 20 Polyamide 6, 20% Glass Fiber FeaturesPA 6 for injection moulding, chemically coupled with 20% glass fiber. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and con..
Flexural Strength	180 MPa	26100 psi	ISO 178
Nilit FRIANYL B63 GV10 Nylon 6 for injection molding, 10% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	180 MPa	26100 psi	ISO 178
Nilit FRIANYL B63 HS-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	180 MPa	26100 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific) LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Flexural Strength	180 MPa	26100 psi
Lehmann & Voss LUVOCOMÂ® 1850/GF/30/TF/15/BK PBT, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec..
Flexural Strength	180 MPa	26100 psi
Lehmann & Voss LUVOCOMÂ® 21-8113 Polyamide 6/6T, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Flexural Strength	180 MPa	26100 psi	ISO 178
Grupo Repol DinalonÂ® A1S25 G25PV0 25% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 66 Mechanical properties are for dry as molded samples.Information provided by Grupo Repol.
Flexural Strength	180 MPa	26100 psi
Lehmann & Voss LUVOCOMÂ® 1105-7594/BL PEEK, with glass fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Strength	180 MPa	26100 psi
Lehmann & Voss LUVOCOMÂ® 50/CF/5/GF/10 Polycarbonate, with carbon fiber and glass fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi..
Flexural Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 5031 PBT (Europe-Africa-Middle East) VALOX 5031 is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage.
Flexural Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DF005 PC LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber.
Flexural Strength	180 MPa	26100 psi	ASTM D790
A. Schulman LUBRILON® 432 30% Glass Fiber Reinforced, PTFE Lubricated PBT Alloy Information provided by A. Schulman.
Flexural Strength	180 MPa	26100 psi	Flexural Strain: 3.1%; ISO 178
Polyplastics Freqtis® C0511A (PPS/LCP), Molding Compound Both base resins (PPS and LCP) exhibit excellent heat resistance, dimensional stability and molding processability. Therefore Freqtis® is widely used for surface mounted electronic components. In ..
Flexural Strength	180 MPa	26100 psi	ASTM D790
Polyram RamSter PF300G6 PBT, 30% Glass Fiber 30% Glass-Fiber reinforced PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	180 MPa	26100 psi	ASTM D638
A. Schulman PP 984 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 984 is a medium impact polypropylene used primarily for automotive parts subjected to impact.Information provided by A. Schulman.
Flexural Strength	180 MPa	26100 psi	ASTM-D790
Toyobo VYLOPET® EMC320R Polyester Resin VYLOPET® is a polyester resin developed specifically for injection molding. Polyester resins have excellent heat resistance, rigidity, chemical resistance, and electric properties. Grade EMC320R ha..
Flexural Strength	180 MPa	26100 psi	ASTM D638
A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Flexural Strength	180 MPa	26100 psi	dry; ISO 178
DSM Novamid® 1010GN2-15 NAT PA6-GF15 FR(17) 15% Glass Reinforced, Flame Retardant, Injection Molding, High Flow
Flexural Strength	180 MPa	26100 psi	ISO 178
DuPont Performance Polymers Crastin® LW9030 BK851 PBT+ASA (Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030 BK851 is a 30% glass fiber reinforced black polybutylene terephthalate blend for injection mol..
Flexural Strength	180 - 270 MPa	26100 - 39200 psi
Alliance N-42SH Neodymium Iron Boron Magnetic Material
Flexural Strength	180 MPa	26100 psi	ISO Data
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Dry) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
Flexural Strength	180 MPa	26100 psi	ISO 178
Polyram RamSter PF321G4 PBT, 20% Glass Fiber, Flame Retardant 20% Glass fiber reinforce, flame retardant PBT for injection molding applications.Information provided by Polyram.