Polymer Property : Flexural Strength = 68.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
Premix Premi-Ject® 1102H Fiberglass Reinforced Thermoset BMC Premi-Ject® 1102H is a fiberglass reinforced thermoset bulk molding compound for coil encapsulation applications.Key features and benefits are:Designed with unique flow properties to encapsulate co..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing 15% PTFE/Silicone and 10% Glass Bead. Added features of this material include: Internally Lubricated.
Flexural Strength	68.0 MPa	9860 psi
Cookson Group Plaskon® SMT-B-1F Epoxy Molding Compound for PBGAs  (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound optimized specifically for PBGA applications. It has the same unique resin system as SMT-B-1, which mi..
Flexural Strength	68.0 MPa	9860 psi
Cookson Group Plaskon® SMT-B-1RC (146.403) Epoxy Molding Compound for PBGAs  (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound optimized specifically for PBGA applications. It has the same unique resin system as SMT-B-1, which mi..
Flexural Strength	68.0 MPa	9860 psi	2 mm/min; ISO 178
Ineos ABS LustranÂ® ABS 650 Injection Molding Grade LustranÂ® ABS 650 has high impact strength, high flow, and is injection molding grade.
Flexural Strength	68.0 MPa	9860 psi	5 mm/min; ISO 178
Gromax BTE70-DN001N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
Flexural Strength	68.0 MPa	9860 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66 LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP f..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS (Asia Pacific) LNP* Lubricomp* ZP001XXP is a compound based on PPE+PS Blend resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON AX06518 ABS LNP* STAT-KON* AX06518 is a compound based on ABS resin containing Stainless Steel. Added features of this material include: Electrically Conductive, Flame Retardant, EMI/RFI Shielding.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON AX06518 ABS (Asia Pacific) LNP* Stat-kon* AX06518 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel. Added features of this material include: Electrically Conductive, Fl..
Flexural Strength	68.0 MPa	9860 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 365 PET (Asia Pacific) Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"".
Flexural Strength	68.0 MPa	9860 psi	ASTM D 790
SABIC Innovative Plastics LNP Stat-kon WX98547 PBT LNP* Stat-kon* WX98547 is a compound based on Polybutylene Terephalate resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SAB..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS (Asia Pacific) LNP* Thermocomp* AX08306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral.
Flexural Strength	68.0 MPa	9860 psi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp PH0600B PA 6 LNP* Thermocomp* PH0600B is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by SABIC..
Flexural Strength	68.0 MPa	9860 psi	3 points and 2 mm/min; ISO 178
Styron Magnumâ„¢ 3453 Acrylonitrile Butadiene Styrene (ABS) MAGNUMâ„¢ 3453 ABS is a general purpose injection molding resin suitable for a wide range of applications.Information provided by DowThis product line was spun off from Dow Chemical to Styron in ..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT (Asia Pacific) LNP* Lubricomp* WBL36L is a compound based on Polybutylene Terephalate resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Flexural Strength	68.0 MPa	9860 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics ValoxÂ® 365 PET Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031".This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AF001H ABS (Asia Pacific) LNP* Thermocomp* AF001H is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MFB429 PP LNP* THERMOCOMP* MFB429 is a compound based on Polypropylene resin containing 10% Glass Fiber, 20% Glass Bead. Added features of this material include: Chemically Coupled, Flame Retardant.
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP YF005 TPEE (Asia Pacific) LNP* Thermocomp* YF005 is a compound based on TPEE resin containing Glass Fiber.
Flexural Strength	68.0 MPa	9860 psi	ISO 178
SABIC Innovative Plastics LNP THERMOTUF CF007IXP PS LNP* Thermotuf* CF007IXP is a compound based on Polystyrene containing glass fiber. Characteristics of this grade are: High Impact.
Flexural Strength	68.0 MPa	9860 psi	DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-750V5T A9T Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High dimensional stability; High fatigue strength; High weather resistance; Good fire behavior; Suitable for vacuum; Good machinability; Contains PTFE; Stre..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
Plenco 7523 Phenolic, Granular, Transfer Molded PLENCO 07523 is a woodflour and cotton flock filled novolac phenolic molding compound, formulated for high impact industrial uses. UL recognized under component file E40654.Information supplied by P..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
Eastman Drystar 0603 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen..
Flexural Strength	68.0 MPa	9860 psi	ISO 178
Denka TP-801 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Flexural Strength	68.0 MPa @Temperature 23.0 °C	9860 psi @Temperature 73.4 °F	EN ISO 178
Ensinger TECASINT 3032 Polyimide, Black, 40% Graphite (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
A. Schulman ComAlloy Comtuf® 525 Polycarbonate/Styrenic Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
Plenco 7321 Phenolic, Nodular, Compression Molded PLENCO 07321 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and excellent dimensional stability. Type ASTM 5948 CFI-5, and UL recognized under compon..