Polymer Property : Flexural Strength = 75.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	75.0 MPa	10900 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nemcon™ H ES DP110/X3 Polycarbonate Alloy Polycarbonate alloy-Thermally conducting, electrically insulating grade with high HDT and improved processability.Information provided by Ovation Polymers
Flexural Strength	75.0 MPa	10900 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nemcon™ H PC DP113/X5 Polycarbonate Polycarbonate-Thermally conducting, electrically insulating grade with high HDT and improved processability.Information provided by Ovation Polymers
Flexural Strength	75.0 - 85.0 MPa	10900 - 12300 psi	ASTM D790-03
Proto3000 Objet Digital Materials™ DM_7220 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
Flexural Strength	75.0 - 110 MPa	10900 - 16000 psi	ASTM D790-03
Proto3000 Objet Digital Materials™ DM_8310 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide..
Flexural Strength	75.0 MPa	10900 psi
Poco Graphite AXF-5Q10W Biomedical Grade Graphite POCO has developed post synthesis modifications to make our graphites more suitable to specific conditions. As a producer of highly technical, specialty materials, POCO also offers design engineerin..
Flexural Strength	75.0 MPa	10900 psi	ISO 178
Nilit FRIANYL A63 HH Nylon 6.6 for injection molding Nylon 6.6 for injection molding, heat and hydrolysis stabilizedInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	75.0 MPa	10900 psi	ISO 178
Nilit FRIANYL B63 ND Nylon 6 Nylon 6, low viscosity, permanently flexible, dry impact resistant (dowels).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	75.0 MPa	10900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP BX05029 SAN (Europe-Africa-Middle East) LNP* Lubricomp* BX05029 is a compound based on Styrene Acrylonitrile resin containing Mineral, Graphite.
Flexural Strength	75.0 MPa	10900 psi	2mm/min; ASTM D790
Kingfa HR-528 Modified ABS Features:UL94 HB @ 1.5-3.2mmExcellent heat resistanceApplications:Automobile partsAutomobile audioDashboard, interior trimAutomobile lamp, mirrorInformation Provided by Kingfa Sci. & Tech. Co., Ltd...
Flexural Strength	75.0 MPa	10900 psi	2 mm/min; ISO 178
Ineos ABS LustranÂ® ABS 250 Injection Molding Grade LustranÂ® ABS 250 has standard impact strength, high flow, and is injection molding grade.
Flexural Strength	75.0 MPa	10900 psi	2 mm/min; ISO 178
Ineos ABS LustranÂ® M205FC ABS Pellets, Injection Molding Grade Injection Molding grade for medical applications (e.g. inhalers, roller clamps, spikes, etc.)/ Biocompatible with up to 30 days human contact duration according to USP Class VI and ISO 10993-1. Food..
Flexural Strength	75.0 MPa	10900 psi	2mm/min; ASTM D790
Kingfa MAC-451PG Electroplating PC/ABS Alloy Features:Excellent balance propertiesGood impact strengthGood processing propertiesSuit for electro-platingApplications:Injection moldingAutomobile license plateWater tank coverComputer and accessor..
Flexural Strength	75.0 MPa @Temperature 22.0 Â°C	10900 psi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® BMC 2600 Unsaturated Polyester UP BMC 2600 is a special BMC with reduced electrical properties. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. Because of its improved..
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
LG Chemical LUCEL FW-700A Friction and Wear Resistant POM, Polymeric Wear Additive LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Flexural Strength	75.0 MPa	10900 psi	ISO 178
Mitsubishi XantarÂ® C CM 206 U Polycarbonate/ABS Blend XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer LNP* LUBRICOMP* KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant
Flexural Strength	75.0 MPa	10900 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS LNP* LUBRICOMP* ZL003 is a compound based on PPE+PS resin containing 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON DSL229 PC (Asia Pacific) LNP* Stat-kon* DSL229 is a compound based on Polycarbonate resin containing PTFE, Stainless Steel. Added features of this material include: Electrically Conductive, Internally Lubricated.
Flexural Strength	75.0 MPa	10900 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP 67002XXH PBT+PC LNP* THERMOCOMP* 67002XXH is a compound based on PBT+PC containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added features inc..
Flexural Strength	75.0 MPa	10900 psi	ISO 178
Styrolution NovodurÂ® M205FC ABS Novodur HD M205FC is an injection molding grade especially suitable for medical applications providing enhanced stiffness.Information provided by Styrolution
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MX88028 PP (Asia Pacific) LNP* Thermocomp* MX88028 is a compound based on Polypropylene resin containing Glass Fiber.
Flexural Strength	75.0 MPa	10900 psi	ISO 178-93
Wellman Wellamid® 22LHI6 XE-NBK1 Impact Modified Nylon 66 Description: Impact Modified Nylon 66Information provided by Wellman.
Flexural Strength	75.0 MPa	10900 psi	15mm/min; ASTM D790
Denka MALECCA K-200 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
Beijing Ranger Chem PBT-201-G0 202 Environmental Protection Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Strength	<= 75.0 MPa	<= 10900 psi	ISO 178
Polykemi AB POLYabs F20 GF17 ABS, Glass Fiber Reinforced Information provided by Polykemi AB
Flexural Strength	75.0 MPa	10900 psi	ASTM D790-03
Proto3000 Objet VeroWhite FullCure830 Rapid Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
Plenco 7591 Phenolic, Pellet, Transfer Molded PLENCO 07591 is a mineral and flock cotton filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco.
Flexural Strength	75.0 - 110 MPa	10900 - 16000 psi	ASTM D790-03
Proto3000 Objet VeroWhitePlus FullCure835 Rigid Opaque Prototyping Polymer Information provided by Proto3000 for their protoyping engineering services.