Polymer Property : Flexural Strength = 77.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	77.0 MPa	11200 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nima™ NH PC151 Polycarbonate Non-Hal FR-PC with High HDT, high impact and improved processability. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accordi..
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
SABIC Innovative Plastics Cycoloy® MC8200 PC+ABS (Asia Pacific)
Flexural Strength	77.0 MPa	11200 psi	5 mm/min; ISO 178
Gromax BTE25-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp.
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
LG Chemical LUPOL HM-4354 Heat Resistant Polypropylene, 35% Glass Fiber/Mineral Filler Reinforced, High Strength, High Modulus LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Internally Lubricated, Healthcare.
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC (Asia Pacific) LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Easy Molding.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS LNP* LUBRICOMP* NXCY620 is a compound based on Cycoloy* XCY620 containing Silicone. Added feature of this material is: Lubricant.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
Solvay TECHNYLÂ® C 236SI PA6, DRY Description: Unreinforced polyamide 6 with high impact strength for injection molding.Available in: Europe and North AmericaProduct Applications: TECHNYLÂ® C 236SI has high impact strength and fle..
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66 LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant.
Flexural Strength	77.0 MPa	11200 psi	ASTM Test
Styrolution TerluranÂ® HH-106 ABS Terluran HH-106 is an injection molding ABS grade with high resistance to heat deformation and impact.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
Plenco 4349 Phenolic, Granular, Transfer Molded PLENCO 04349 is a heat resistant, mineral filled phenolic molding compound offering optimized cure characteristics, and excellent heat resistant properties. PLENCO 04349 is also formulated to offer ..
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
Plenco 7080 Phenolic, Nodular, Compression Molded PLENCO 07080 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength properties along with outstanding resistance to cracking and degradation from soap and de..
Flexural Strength	77.0 MPa	11200 psi	ISO 178
Unitika TERRAMAC TE-1030 Polylactic Acid (PLA) High-Impact grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
Lubrizol ESTALOC® 59300 Ester-Type, Reinforced Engineering Thermoplastic (European Grade) Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extensio..
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
Eastman Spectar® 14471 Copolyester Spectar copolyester extrudes into plastic sheet that is sparkling clear, tough, chemically resistant, odor-free, versatile, easy to work with and affordable. Its toughness allows fabricators to use ..
Flexural Strength	77.0 MPa @Thickness 3.17 mm	11200 psi @Thickness 0.125 in	tangent; chs 0.05 in/min; ASTM D790
Diamond Polymers ABS 3500 EF-Low Gel Extrusion Grade, Low Gel Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Flexural Strength	77.0 MPa @Thickness 6.35 mm	11200 psi @Thickness 0.250 in	tangent; chs 2.5 in/min; 100 mm SL; ASTM D790
Diamond Polymers ABSPC 7330-1801H ABS/PC Injection Molding Grade Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
Eurostar Staramide P1000IX2 PA6, Impact Modified, Injection Molded Staramide P1000IX2 is an Impact Modified, Polyamide 6 Injection Molding Resin (also known as P1000HI010 or Star X 2010)Information provided by Eurostar.
Flexural Strength	77.0 MPa	11200 psi	ISO 178
Eurostar Starglas FF006 HDPE, Glass Fiber Filled Starglas FF004 is a Glass Fiber Reinforced High Density Polyethylene Resin (also known as Starglas PE HE 30V)Information provided by Eurostar.
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
A. Schulman ComAlloy Comtuf® 410 Polycarbonate/Polyester Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
Resinoid 1320 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Flexural Strength	77.0 MPa	11200 psi	ISO 178
SABIC Innovative Plastics LNP Thermocomp TX88477 PU LNP* Thermocomp* TX88447 is a compound based on Polyurethane resin containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.