Polymer Property : Tensile Strength at Break = 10.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	10.0 MPa	1450 psi	ISO 527
Polimeri Europa Eraclene® MS 80 U High Density Polyethylene - Injection Molding Eraclene MS 80 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application. This grade has a narrow molecular weight distribution and a hig..
Tensile Strength at Break	<= 10.0 MPa	<= 1450 psi	ISO/R527
Polykemi AB POLYelast TPE Z600A Thermoplastic Elastomer, SEBS-based, Co-injection Grade Information provided by Polykemi AB
Tensile Strength at Break	10.0 MPa	1450 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCD835 PPE-TPE Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end..
Tensile Strength at Break	10.0 MPa	1450 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCD835 PPE-TPE Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end..
Tensile Strength at Break	10.0 MPa	1450 psi	ASTM D412
Teknor Apex MonpreneÂ® MP-2156E Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	10.0 MPa	1450 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific) Noryl PX500 is an unfilled modified polyphenylene ether resin capable of multiple conversion routes. This resin is designed for lower odor during conversion than many standard modified PPE resins. ..
Tensile Strength at Break	10.0 MPa	1450 psi	ASTM D412
Teknor Apex Telcar® TL-1140E Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P..
Tensile Strength at Break	10.0 MPa	1450 psi	500mm/min; ASTM D638 Type IV Specimen
Westlake EMAC® Plus SP1358 21.5% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® Plus SP1358 is a 21.5% EMA copolymer containing slip and antiblock. This resin is designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low..
Tensile Strength at Break	10.0 MPa	1450 psi	500mm/min; ASTM D638 Type IV Specimen
Westlake EMAC® SP2207 20% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2207 is a 20% EMA copolymer designed for extrusion coating, tie-layers, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficient of friction..
Tensile Strength at Break	10.0 MPa	1450 psi	at max load; ASTM D638
A. Schulman CP775-01 Molding Grade, Low Density Polyethylene DescriptionCp 755-01 is a molding grade, low-density polyethylene. ApplicationCP 755-01 meets the specification contained in FDA Regulation 177.1520 for food contact applications.Information provid..
Tensile Strength at Break	10.0 MPa	1450 psi	at max load; ASTM D638
A. Schulman CP775-01 Molding Grade, Low Density Polyethylene DescriptionCp 755-01 is a molding grade, low-density polyethylene. ApplicationCP 755-01 meets the specification contained in FDA Regulation 177.1520 for food contact applications.Information provid..
Tensile Strength at Break	>= 10.0 MPa	>= 1450 psi	ISO R 527
Fainplast Compounds CKL 80/E Flexible PVC, Sheathing Lead Free Under sheathing
Tensile Strength at Break	>= 10.0 MPa	>= 1450 psi	ISO R 527
Fainplast Compounds FK 70 Flexible PVC, Insulation Lead Free General purposes
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Fainplast Compounds GS 55/UV Flexible PVC, Injection Molding for Transparent Technical Items Outdoor protections for switches anti-UV
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Fainplast Compounds GS 56 Flexible PVC, Injection Molding for Footwear Vamp boots
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Fainplast Compounds GS 66/BT Flexible PVC, Injection Molding for Footwear Soles for cold climates
Tensile Strength at Break	>= 10.0 MPa	>= 1450 psi	ISO R 527
Fainplast Compounds CKL 66 Flexible PVC, Sheathing Lead Free General purposes
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Fainplast Compounds PH 60 Flexible PVC, Transparent Extrusion Transparent profiles
Tensile Strength at Break	10.0 MPa	1450 psi	MSZ ISO 527
BorsodChem ONGRO CPE 4002 N Chlorinated Polyethylene IMPACT MODIFIER FOR PVChigh impact resistancegood processabilityexcellent weather resistanceELASTOMERSvariety of cross-linking technologiesexcellent ozone- and weather resistanceexcellent chemical r..
Tensile Strength at Break	10.0 MPa	1450 psi	ASTM D638
Braskem EB 853/72 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Lamination film; general purpose; automatic packaging of solids products (FFS). Informatio..
Tensile Strength at Break	10.0 MPa	1450 psi	ASTM D3574
3M 394 Vent Tape 3M™ Vent Tape 394 is a non-woven, synthetic backing that meets most typical outgassing requirements for foam-in-place insulation processes in appliance and other industries and contains fungicide f..
Tensile Strength at Break	10.0 MPa	1450 psi	ASTM D638
Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness) AZDEL SuperLite® SL550700-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Addiplast Addilene J 522 K20 Polypropylene Copolymer High densityInformation provided by Addiplast.
Tensile Strength at Break	>= 10.0 MPa	>= 1450 psi
Beijing Evergrow Resources PTFE, 60% Bronze Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with filler. Broadly speaking PTFE compounds have t..
Tensile Strength at Break	10.0 MPa	1450 psi	ASTM D412
Teknor Apex Monprene® MP-2604B Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Fainplast Compounds PH 58/AL Flexible PVC, Transparent Extrusion Pipes according to dir. 2002/72/CE
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R 527
Fainplast Compounds PM 6316/AM Flexible PVC, Lead Free Anti-mould profiles
Tensile Strength at Break	10.0 MPa	1450 psi	ISO R527
Total Lacqtene® 1025 FH 24 LDPE blown film  (discontinued **) Radical polyethylene made by high pressure tubular process. Slip and antiblock formulated grade for good transparent thin films. Advised temperature profile : 150 to 190°C.Information provided prov..