Polymer Property : Tensile Strength at Break = 115 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	115 MPa	16700 psi	ISO 527
Nilit FRIANYL B63 SG-GV20 Nylon 6 for injection molding, 20% glass fiber reinforced Nylon 6 for injection molding, light impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	115 MPa	16700 psi
Radici Radilon® S RV330 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Strength at Break	115 MPa @Temperature 23.0 °C	16700 psi @Temperature 73.4 °F	ISO 527-2/5
PolyOne Bergamid™ A700 G20 HW UF Polyamide 66 (Nylon 66) Information provided by PolyOne
Tensile Strength at Break	115 MPa @Temperature 23.0 °C	16700 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Crastin® LW9320 BK851 PBT  (Unverified Data**) Crastin® LW9320 BK851 is a 20% glass fiber reinforced, black polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional stability and low warp..
Tensile Strength at Break	115 MPa	16700 psi	ISO 527
Grupo Repol DinalonÂ® B1S25 G10B20 PA6 10% Glass Fiber, 20% Glass Beads Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Tensile Strength at Break	115 MPa	16700 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® B 218 V30 Black 21 N PA66, 30% glass fiber, Conditioned Description: Copolyamide PA66/6, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Available in: Asia Pacific and EuropeProduct Applications: TECHNYLÂ® B 218 V30 is used i..
Tensile Strength at Break	115 MPa	16700 psi	ISO 527 Type 1A
Solvay TECHNYLSTARâ„¢ S 216 V35 PA6, 35% glass filled, Conditioned Description: TECHNYLSTAR polyamide, reinforced with 35% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Europe and North AmericaProduct Applications..
Tensile Strength at Break	115 MPa	16700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100R PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Strength at Break	115 MPa	16700 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT (Asia Pacific) LNP* LUBRICOMP* WFL34H is a compound based on Polybutylene Terephalate resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	115 MPa	16700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
Tensile Strength at Break	115 MPa	16700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM HU2100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
Tensile Strength at Break	115 MPa	16700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 8032UX PBT+PET (Asia Pacific) VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin..
Tensile Strength at Break	115 MPa	16700 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific) LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia P..
Tensile Strength at Break	115 MPa	16700 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP KF006XXC Acetal Copolymer (Asia Pacific) LNP* Thermocomp* KF006XXC is a compound based on Acetal Copolymer resin containing Glass Fiber.
Tensile Strength at Break	115 MPa	16700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON MV007U PP (Europe-Africa-Middle East) LNP* VERTON* MV007U is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized.
Tensile Strength at Break	115 MPa	16700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2110R PEI (Asia Pacific) 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Strength at Break	115 MPa	16700 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	115 MPa	16700 psi	ISO 527-93
Wellman Wellamid® GF14-60 XE-NBK1 Nylon 6, 14% Glass Fiber Reinforced All information provided by Wellman Engineered Resins.
Tensile Strength at Break	115 MPa	16700 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30 Product Description: Grilamid 1SBVX-30H LDS black is a 30% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno..
Tensile Strength at Break	115 MPa	16700 psi	ISO 527-1/-2
DSM Stanyl® 46HF4130 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Tensile Strength at Break	115 MPa	16700 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6  (Unverified Data**) 35% Glass Reinforced Heat Stabilized Polyamide 6 Zytel 73G35HSL BK262 is a 35% glass fiber reinforced heat stabilized black polyamide 6 resin for injection molding.Information provided by DuPont Per..
Tensile Strength at Break	115 MPa	16700 psi	ISO 527
Eurotec® Tecopet® PT70 GR15 NL100 PR PET, 15% glass fiber reinforced, heat stabilized, natural, fast crystallization grade Information provided by Eurotec®
Tensile Strength at Break	115 MPa	16700 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® XE 5051 (BGZ-40 FC) PA6-GF40 Product description: Grilon XE 5051 is a impact modified, heat stabilized PA 6 injection molding grade with 40% glass fiber reinforcement. Grilon XE 5051 has the following important properties: High..
Tensile Strength at Break	115 MPa @Temperature -40.0 °C	16700 psi @Temperature -40.0 °F	ISO Data
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry) Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the..
Tensile Strength at Break	115 MPa	16700 psi	ASTM D638
Beijing Chemical Industry KAIFA® HN201-G20 PA6 Resin 20% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break	115 MPa	16700 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® A3 GF 10 (2852) PA 6.6 Dry, 10% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break	115 MPa	16700 psi	0.2 in/min; ASTM Test
BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in..
Tensile Strength at Break	115 MPa	16700 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable..