Polymer Property : Tensile Strength at Break = 11500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	79.5 MPa	11500 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ MF 1200 A 40 HS Natural Polyamide 66 (Nylon 66) The Nymax® MF 1200 Series of mineral-reinforced nylon 6/6 compounds have been specifically engineered to provide an excellent balance of physical property performance, toughness, chemical resistanc..
Tensile Strength at Break	79.0 MPa	11500 psi	ASTM D638
SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific) LNP* Konduit* ITF2B is a compound based on Nylon 6/12 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Tensile Strength at Break	79.0 MPa	11500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer LNP LUBRICOMP* KFL32R is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE. Added feature of this material is: Easy Release, Wear Resistant.
Tensile Strength at Break	79.0 MPa	11500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Asia Pacific) LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing Aramid, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	79.0 MPa	11500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 LNP* LUBRICOMP* RAL22S is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.
Tensile Strength at Break	79.0 MPa	11500 psi	ISO 527
Solvay TECHNYLSTARâ„¢ A205 F Natural S PA66, Eh 50 TECHNYLSTAR A205 F NATURAL S is a polyamide 6.6 with low viscosity for fast cycle molding.Colors: it is supplied in natural color.Available in: Latin America and North AmericaMain Properties: High F..
Tensile Strength at Break	79.0 MPa	11500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX88514 PA 66 LNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). AddedLNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). A..
Tensile Strength at Break	79.0 MPa	11500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 457 PBT 6.5% GR PBT, UL94 V-0/5V.
Tensile Strength at Break	79.0 MPa	11500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific) LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
Tensile Strength at Break	79.0 MPa	11500 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	79.0 MPa	11500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber.
Tensile Strength at Break	79.0 MPa	11500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP 30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
Tensile Strength at Break	79.0 MPa	11500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Asia Pacific) 30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
Tensile Strength at Break	79.0 MPa	11500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Tensile Strength at Break	79.0 MPa	11500 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Europe-Africa-Middle East) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e..
Tensile Strength at Break	79.0 MPa	11500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Europe-Africa-Middle East) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can..
Tensile Strength at Break	79.3 MPa	11500 psi	ASTM D638
A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	79.3 MPa	11500 psi	ASTM D638
A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	79.3 MPa	11500 psi	ASTM D638
Chase Plastics CP Pryme® NN300HL (Dry) Nylon 66, Heat Stabilized, Lubricated Features: General purposeHeat stabilizedLubricatedForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break	79.0 MPa	11500 psi	ASTM D638
Unitika AX-1500W Dry Characteristics: A resin succeeding the advantages of AX1500 resin and containing titanium oxide at high concentration. Improved drastically in light reflection and blocking properties, aimed at dis..
Tensile Strength at Break	79.3 MPa	11500 psi	ASTM D638
A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	79.0 MPa	11500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOTUF WF003I Polyester, TP LNP THERMOTUF* WF003I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.