Polymer Property : Tensile Strength at Break = 12500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	86.1 MPa	12500 psi	ASTM D638
PolyOne Stat-Tech™ CTX-1125 Natural Acrylonitrile Butadiene Styrene (ABS) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Tensile Strength at Break	86.0 MPa	12500 psi	ISO.527 DIN.53455
Omnia Plastica Akulon® PA 66.6 Akulon GX - Dry Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool..
Tensile Strength at Break	86.0 MPa	12500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific)
Tensile Strength at Break	86.0 MPa	12500 psi
Radici Radilon® S ERV3808K (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Strength at Break	86.2 MPa	12500 psi	ASTM D638
Polymer Resources PPX/NY G10 PPO/Nylon 66 Alloy , 10% Glass Reinforced Polyphenylene Oxide/Nylon 66 Alloy , 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Tensile Strength at Break	86.0 MPa <br>@Temperature 23.0 °C	12500 psi <br>@Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66  (Unverified Data**) Minlon® 11C40 BKB086 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength at Break	86.0 MPa	12500 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp ZFL34XXC PPE+PS LNP LUBRICOMP* ZFL34XXC is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for..
Tensile Strength at Break	86.0 MPa	12500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY.
Tensile Strength at Break	86.0 MPa	12500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp DFZ42P PC LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the..
Tensile Strength at Break	86.0 MPa	12500 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber.
Tensile Strength at Break	86.3 MPa	12500 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® GR-4020L ABS, Glass Filled ABS/GF material that is used in printer LBP fuserInformation provided by Samsung Cheil Industries.
Tensile Strength at Break	86.0 MPa	12500 psi	ASTM D638
Sumitomo Bakelite North America E 8940SG Electrical Encapsulation Grade Epoxy Mineral reinforced epoxy molding compound formulated for the encapsulation of electronic devices requiring high quality, exceptional reliability, and outstanding moldability. USES: Passive electron..
Tensile Strength at Break	86.0 MPa	12500 psi	ASTM D638
Sumitomo Bakelite DurezÂ® 32245 Phenolic, Injection Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit..
Tensile Strength at Break	86.0 MPa	12500 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66  (Unverified Data**) 40% Mineral Reinforced Polyamide 66 Minlon 11C40 BKB086 is a 40% mineral reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers..