Polymer Property : Tensile Strength at Break = 13100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	STN EN ISO 527-2
Plastcom SLOVAMID 6 GF 15 T 25 Polyamide 6, 15% Glass Fiber, 25% Micronized Talc FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form / no screw after co..
Tensile Strength at Break	<= 90.0 MPa	<= 13100 psi	ISO/R527
Polykemi AB SCANAMID 66 A12^ Q40 Nylon 66, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	90.0 MPa	13100 psi	50 mm/min; ISO 527-1,2
Qualchem Danamid FCP-40 Polyamide 6, 40% Carbon Fiber Filled with milled carbon fiber, antistatic and conductiveInformation provided by Qualchem Zrt.
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Nilit FRIANYL A63 H Nylon 6.6 for injection molding Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	90.0 MPa	13100 psi	ASTM D683
Loxim 220 01HB Polybutylene Terephthalate Information provided by Loxim Industries
Tensile Strength at Break	90.0 MPa	13100 psi	Conditioned; ISO 527-1/-2
Lanxess DurethanÂ® BKV 25 H2.0 LT 904040 Nylon 6, 25% Glass Fiber PA 6, injection molding grade, 25% glass fibers, good heat-ageing resistance, laser-weldable
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527-1/-2
Mitsubishi XantarÂ® MX 1082 Polycarbonate-20% Glass Reinforced XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 548B2 V15 PA66, 15% glass fiber, DRY Description: TECHNYLÂ® A 548B2 V15 is a polyamide 6.6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits: Th..
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 1000RV PEI Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem DH1004F PEI (Europe-Africa-Middle East) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Europe-Africa..
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU1004 PEI (Asia Pacific) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f..
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU1004 PEI (Europe-Africa-Middle East) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f..
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp BX06088 SAN (Europe-Africa-Middle East) LNP* THERMOCOMP* BX06088 is a compound based on Styrene Acrylonitrile Blend resin containing Carbon Fiber. Added features include: Electrically Conductive.This data was supplied by SABIC-IP for the..
Tensile Strength at Break	90.0 MPa	13100 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI LNP* THERMOCOMP* EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare.
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS (Europe-Africa-Middle East) Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl ..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 216 V15 Black 21N PA66, 15% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 15% of glass fiber, for injection molding.Available in: Asia PacificProduct Applications: TECHNYLÂ® A 216 V15 is used in all sectors of industry, offer..
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WF0049XP PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF0049XP is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength at Break	90.0 MPa	13100 psi	dry; ISO 527
Ter Hell Plastic Terez® PA 6 7751 TGF 15 GL Polyamide 6, 15% Glass Fiber Description: Medium viscosity, dry impact resistant PA 6, 15% glass fiber reinforced and improved surface gloss.Application: For molding parts with good stiffness and high dimensional stability.In..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527-1
Vyncolit X7255 Glass Fiber Reinforced Novolac Phenolic Novolac resin based, glass fiber and glass beads reinforced. Very easy to transform in complex shapes. Excellent mechanical and thermal properties. Higher isotropic properties and good dimensional s..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527-1/-2
Unitika CX-2500 PA6, Dry Transparent nylonInformation provided by Unitika Ltd.
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527-1/-2
DSM Akulon® K222-KGMV14 Nylon 6-25% Glass and Mineral Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break	90.0 MPa	13100 psi	50 mm/min; ISO 527
Eurostar Staramide BK8 PA6, 40% Mineral Fiber Filled, Injection Molded Staramide BK8 is a 40% Mineral Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Eurotec® Tecoform® PO20 GR10 NL HS POM, 10% glass fiber reinforced, heat stabilized, natural Information provided by Eurotec®
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Eurotec® Tecolen® HP10 GR30 NL HS PPCP, 30% glass fiber reinforced, heat stabilized, natural Information provided by Eurotec®
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Eurotec® Tecomid® NA40 MR30 NL PA 6.6 30% mineral reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 MR 409 HWCP 40% Mineral Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	90.0 MPa	13100 psi
LATI Latilub 67-10STE21 G/20 PA66, 20% Glass Fiber Reinforced, Silicone/PTFE Filled Self-lubricating product based on Polyamide 66 (PA66), impact modified. Silicone / PTFE. Toughened. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ameri..
Tensile Strength at Break	90.0 MPa	13100 psi
LATI Latilub 95-15T PSU, PTFE Filled Self-lubricating product based on Polysulfone (PSU). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici ..