- Polymer Property : Tensile Strength at Break = 16000 psi
Polymer Property : Tensile Strength at Break = 16000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | |
|
Plastcom SLOVAMID 66 GF 20 GF 10 PA66, 20% glass fibre, glass beads
FeaturesPA 66 chemically reinforced with 20% glass fibre and with the content of 10 % glass beads. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical properties can b..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-2 |
|
PolyOne OnForce™ LFT LF5200-5001 EM Natural Polyolefin, Unspecified
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
|
|||
| Tensile Strength at Break |
110
MPa <br>@Temperature 23.0 °C
|
16000
psi <br>@Temperature 73.4 °F
|
ISO 527 |
|
DuPont Performance Polymers Rynite® RE19051 BK507 PET
(Unverified Data**)
Rynite® RE19051 BK507 is a 40% glass and mineral reinforced, flame retardant, polyethylene terephthalate black resin.Information provided by DuPont Performance Polymers
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DSM Akulon® Ultraflow™ K-FHGM24 Nylon 6-30% Glass and Mineral Reinforced (European Grade) (Dry)
(discontinued
The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527-1/-2 |
|
Lanxess Durethan® AKV 30 H2.0 901510 Nylon 66, 30% Glass Fiber
PA 66, injection molding-grade, 30% glass fibers, good heat-ageing resistance
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | |
|
LATI Latishield 85-08A G/20 PES, Steel/Glass Fibers
EMI shielding product based on Polyether Sulfone (PES). Steel fibers. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati ..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics LNP Stat-kon AE004E ABS
LNP* Stat-Kon* AE004E is an ABS compound containing Glass Fiber. Characteristics of this grade are Statically Conductive and Easy Molding.This data was supplied by SABIC-IP for the Americas region...
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Valox® 412 PBT (Europe-Africa-Middle East)
VALOX 412 is 20% glass reinforced PBT injection moulding resin. Applications: Spotlights, appliance housings and handles.
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Valox® K4560 PBT
30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics Valox® VX5022 PBT (Europe-Africa-Middle East)
VALOX VX5022 is a 20% glass fibre reinforced PBT+PC blend with low warpage characteristics. This grade is 5021 with reduced warpage.
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics NORYL PX4605 PPE+PS
PPE+PS blend. 20% Glass reinforced. High heat. Dimensional stability. Suitable for automotive and E/E applications.
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DSM Akulon® K224-G6U (Cond.) 33% Glass Reinforced Nylon 6 (North America)
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DSM Arnite® TV4 240 S PBT-20% Glass Reinforced (European and Asian Grade)
Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame ..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | dry; ISO 527-1/-2 |
|
EMS-Grivory Grivory® EBV-15H black 9697 PA6-GF15
Product description: Grilon EBV-15H black 9697 is a high viscosity, heat stabilized PA6 extrusion blow molding grade with 15% glass fibers. Grilon EBV-15H black 9697 has the following important prop..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DSM Stanyl® TW271F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond)
Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DuPont Performance Polymers Crastin® SK692FR BK507 Polybutylene Terephthalate (PBT)
(Unverified Data**)&l
15% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin® SK692FR is a 15% glass reinforced flame retardant polybutylene terephthalate for injection moulding.Information provided by ..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | conditioned; ISO 527-1/-2 |
|
EMS-Grivory Grivory® BGZ-30 PA6-GF30
Product description: Grilon BGZ-30 is a normal viscosity, heat stabilized and impact modified PA 6 injection molding type with 30% glass fibers. Grilon BGZ-30 has the following important properties:..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | 50mm/min; ISO 527 |
|
Teijin Panlite® BS-8110R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin
CF 10% reinforced grade, meeting UL 94 V-2. it is compounded with fluorine powder to improve friction and abrasion resistance and also exhibits a mold release property, maintaining excellent charact..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DSM Akulon® K-FHGM24 (Dry) 30% Glass/Mineral Reinforced, Nylon 6 (North America)
(discontinued **)
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
|
DuPont Performance Polymers Crastin® SK612SF NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)&l
15% Glass Reinforced Low Viscosity Polybutylene Terephthalate Developed for Super Fast Production Crastin SK612SF is a 15% glass fiber reinforced low viscosity polybutylene terephthalate for injecti..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® 3412R PC
20% GR, provides improved mechanical properties and UL94 V-1 rated at 0.058"". Internal mold release added.
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Europe-Africa-Middle East)
Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable..
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527-1/-2 |
|
Lanxess Durethan® BKV 35 H2.0 901510 Nylon 6, 35% Glass Fiber
PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistanceApplication Examples: automotive structures
|
|||
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO R 527 |
|
Addiplast Addinyl B2 ZV30 Nylon 6, 30% Glass Filled
Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
|
|||