Polymer Property : Tensile Strength at Break = 18900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi
Plastcom SLOVAMID 66 GF 15 T 25 PA66, 15% glass fibre, 25% talc FeaturesChemically reinforced with 15% glass fibre and talc, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical in..
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-2
PolyOne OnForce™ LFT PP-60LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Tensile Strength at Break	130 MPa	18900 psi	ISO 527
Nilit FRIANYL A63 HH-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
Lanxess Pocan® T 7331 POS151 000000 PBT + PET, 30% Glass Fiber  (discontinued **) PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Tensile Strength at Break	130 MPa	18900 psi	ISO 527
Nilit FRIANYL B63 H-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	130 MPa	18900 psi	5 mm/min; ISO 527-1,-2
Lanxess DurethanÂ® BKV 15 H.3 DUS008 000000 Nylon 6, 15% Glass Fiber PA 6, 15% glass fibers, injection molding, heat-ageing stabilizedInformation provided by LANXESS.
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
Lanxess PocanÂ® BF 4235 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, flame retardant
Tensile Strength at Break	130 MPa	18900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK (Europe-Africa-Middle East) LNPLUBRICOMP LFL36 is a compound based on Polyetheretherketone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.This data was supplied by SABIC-IP for the Europe-A..
Tensile Strength at Break	130 MPa	18900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2200N PEI 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	130 MPa	18900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2200N PEI (Europe-Africa-Middle East) 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	130 MPa	18900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 4631 PBT (Europe-Africa-Middle East) VALOX 4631 is a 30% glass reinforced, flame retarded PBT injection moulding resin with good electrical properties and excellent mechanical properties.
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-93
Wellman Wellamid® FRGF1850-BK1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant All information provided by Wellman Engineered Resins.
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
DSM Akulon® K224-HG7 Nylon 6-35% Glass Reinforced (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break	130 MPa	18900 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® BG-40 HM PA6-GF40 Product description: Grilon BG-40 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 40% glass fibers. Grilon BG-40 HM has the following important prop..
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
DuPont Performance Polymers Crastin® CE15330 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l 30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin® CE15330 NC010 is a 30% glass reinforced flame retardant polybutylene terephthalate molding resin. It is recognized as UL94 V..
Tensile Strength at Break	130 MPa	18900 psi	ISO 527
Eurotec® Tecopet® PT70 GR20 NL100 PR PET, 20% glass fiber reinforced, heat stabilized, natural, fast crystallization grade Information provided by Eurotec®
Tensile Strength at Break	130 MPa	18900 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® TRV-4X9 PAMACM12-GF40 Product description: Grilamid TRV-4X9 is an amorphous, cycloaliphatic polyamide with 40% glass fibre reinforcement. Grilamid TRV-4X9 characterises itself through the following features: Very low shr..
Tensile Strength at Break	130 MPa	18900 psi	ISO R 527
Addiplast Addinyl A2 V15 Nylon 66, 15% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast.
Tensile Strength at Break	130 MPa	18900 psi	0.2 in/min; ASTM Test
BASF Petra® 130 FR 30% Glass Filled PET Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also avail..
Tensile Strength at Break	130 MPa	18900 psi	0.2 in/min; ASTM Test
BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combin..
Tensile Strength at Break	130 MPa <br>@Temperature 170 - 180 °C,<br> Time 1.80e+7 sec	18900 psi <br>@Temperature 338 - 356 °F,<br> Time 5000 hour	5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Akro-Plastic Akromid® T1 GF 40 (3464) PPA Dry, 40% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Tensile Strength at Break	130 MPa	18900 psi
Radici Radilon® A RV300R (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
Lanxess Pocan® B 3235 XF 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, improved flowability
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
Lanxess Pocan® DP B 3235 XF 901510 PBT, 30% Glass Fiber  (discontinued **) PBT, 30% glass fibers, injection molding, improved flowability